DIN 1725-1 Grade 3.0515 F

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlMn1 is an Al-Mn alloy, which belongs to the nature-hard aluminum materials. Mn increases the strength compared with pure aluminium, but it does not impair the corrosion resistance. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occur by cold forming. It is very well formable, very well corrosion resistant and weldable. In these characteristics it resembles the pure aluminium, but with the attainable strength it exceeds this. The alloy AlMn1 has a increased heat resistance compared with pure aluminium, as result of the of the Mn-additive (inhibits recrystallisation). Application: In the building industry for roofings, as outer skin of buildings, in the apparatus and tank construction as heat exchanger (bank of tubes, profiles, gilled pipes, sheet metals), for radiators, air conditioning systems, pipings for compressed gas tanks, for tanks according VdTUEV Werkstoffblaetter, as antennas for radio relay link and satellite communication (mirror) for technical flow pressed parts, for solid rivets, for generally metal-describe, in food industry (including commercial devices), in the construction of vehicles (including tank cars) and as packing (sheet metal packings generally).

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.73 g/cm³ Show Material materials with Densidad of 2.73 g/cm³	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	2.73 g/cm³ Show Material materials with Densidad of 2.73 g/cm³	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 3000 Series Aluminium
Dureza Brinell		33.0 [-] Show Material materials with Dureza Brinell of 33.0 [-]	F	EN 573-3, EN 570
	20.0 °C	25.0 [-] Show Material materials with Dureza Brinell of 25.0 [-]	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Rod
	20.0 °C	30.0 [-] Show Material materials with Dureza Brinell of 30.0 [-]	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Tube
Elongación		20.0 % Show Material materials with Elongación of 20.0 %	F	EN 573-3, EN 755		A50
		25.0 % Show Material materials with Elongación of 25.0 %	F	EN 573-3, EN 755		A100
	20.0 °C	15.0 % Show Material materials with Elongación of 15.0 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube	A10
	20.0 °C	17.0 % Show Material materials with Elongación of 17.0 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube
Módulo de cizallamiento		26.1 GPa Show Material materials with Módulo de cizallamiento of 26.1 GPa	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	24.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 24.0 - 26.5 GPa	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube
Módulo elástico		69.5 GPa Show Material materials with Módulo elástico of 69.5 GPa	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	60.0 - 65.0 GPa Show Material materials with Módulo elástico of 60.0 - 65.0 GPa	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 3000 Series Aluminium
Resistencia a la tracción		90.0 MPa Show Material materials with Resistencia a la tracción of 90.0 MPa	F	EN 573-3, EN 485
		95.0 MPa Show Material materials with Resistencia a la tracción of 95.0 MPa	F	EN 573-3, EN 755
		120.0 - 220.0 MPa Show Material materials with Resistencia a la tracción of 120.0 - 220.0 MPa	F	EN 573-3, EN 1715-3
	20.0 °C	95.0 MPa Show Material materials with Resistencia a la tracción of 95.0 MPa	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape
Calor específico		893.0 J/(kg·K) Show Material materials with Calor específico of 893.0 J/(kg·K)	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	893.0 J/(kg·K) Show Material materials with Calor específico of 893.0 J/(kg·K)	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube
Coeficiente de dilatación térmica	20 °C	2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	100 °C	2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Conductividad térmica	20.0 °C	160.0 - 200.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 - 200.0 W/(m·K)	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1386, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Temperatura de fusión		645.0 - 655.0 °C Show Material materials with Temperatura de fusión of 645.0 - 655.0 °C	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica	20.0 °C	22000000.0 - 28000000.0 S/m Show Material materials with Conductividad eléctrica of 22000000.0 - 28000000.0 S/m	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1386, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Resistividad eléctrica		3.57e-08 - 4.55e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.57e-08 - 4.55e-08 Ω·m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.1 % Show Material materials with Cobre of 0.1 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1386, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Cromo	0.1 % Show Material materials with Cromo of 0.1 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1386, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Hierro	0.7 % Show Material materials with Hierro of 0.7 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube
	0.70 % Show Material materials with Hierro of 0.70 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Magnesio	0.3 % Show Material materials with Magnesio of 0.3 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1386, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Manganeso	0.9 - 1.5 % Show Material materials with Manganeso of 0.9 - 1.5 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1386, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Silicona	0.5 % Show Material materials with Silicona of 0.5 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1386, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Titanio	0.1 Show Material materials with Titanio of 0.1	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Profile, Rod, Tube
Zinc	0.2 % Show Material materials with Zinc of 0.2 %	F	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1386, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube

Technological properties

Property

Workability

Good workability.