DIN 1725-1 Grade 3.0525 O

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlMn1Mg0,5 is similarly to AlMn1 in its properties. It reaches strength up to F 25. The alloy belongs to the nature-hard aluminum materials. A strength increase can only occure by cold forming. It is very well hot and cold formable and is suitable to the deep-drawing (no lappet formation). The alloy AlMn1Mg0,5 is very well corrosion resistant and is sea water steady. As semi-finished material it is present in accordance with DIN 1788 and DIN 1745 only as sheet metal or strip. Application: Mainly in the packing for cans (lower parts), for menu bowls, for covers. In the building industry for claddings, roofings, for sun protection facilities (roller schutter, lamella net curtain) and for roll gates as well as for flexible pipes and in the construction of vehicles.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³	O	EN 573-3, EN 1396, EN 485, EN 546
	20.0 °C	2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Rod

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 3000 Series Aluminium
Dureza Brinell		33.0 [-] Show Material materials with Dureza Brinell of 33.0 [-]	O	EN 573-3, EN 485
	20.0 °C	35.0 [-] Show Material materials with Dureza Brinell of 35.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Rod
Elongación		8.0 % Show Material materials with Elongación of 8.0 %	O	EN 573-3, EN 546		A50
		9.0 % Show Material materials with Elongación of 9.0 %	O	EN 573-3, EN 546		A50
		10.0 % Show Material materials with Elongación of 10.0 %	O	EN 573-3, EN 546		A50
		12.0 % Show Material materials with Elongación of 12.0 %	O	EN 573-3, EN 1396, EN 485		A50
		14.0 % Show Material materials with Elongación of 14.0 %	O	EN 573-3, EN 1396, EN 485		A50
		16.0 % Show Material materials with Elongación of 16.0 %	O	EN 573-3, EN 1396, EN 485		A50
		19.0 % Show Material materials with Elongación of 19.0 %	O	EN 573-3, EN 485		A50
	20.0 °C	13.0 % Show Material materials with Elongación of 13.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	15.0 % Show Material materials with Elongación of 15.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	17.0 % Show Material materials with Elongación of 17.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Rod	A10
	20.0 °C	22.0 % Show Material materials with Elongación of 22.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	23.0 % Show Material materials with Elongación of 23.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Rod
Módulo de cizallamiento	20.0 °C	26.5 Show Material materials with Módulo de cizallamiento of 26.5	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Rod
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	O	EN 573-3, EN 1396, EN 485, EN 546
	20.0 °C	65.0 GPa Show Material materials with Módulo elástico of 65.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Rod
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 3000 Series Aluminium
Resistencia a la tracción		115.0 - 165.0 MPa Show Material materials with Resistencia a la tracción of 115.0 - 165.0 MPa	O	EN 573-3, EN 1396, EN 485
	20.0 °C	120.0 - 165.0 MPa Show Material materials with Resistencia a la tracción of 120.0 - 165.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Rod
	20.0 °C	125.0 - 165.0 MPa Show Material materials with Resistencia a la tracción of 125.0 - 165.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, EN 546	Flat
Ángulo de flexión a 180°		1.0 °/t Show Material materials with Ángulo de flexión a 180° of 1.0 °/t	O	EN 573-3, EN 485
Ángulo de flexión a 90°		0.5 °/t Show Material materials with Ángulo de flexión a 90° of 0.5 °/t	O	EN 573-3, EN 485
		1.0 °/t Show Material materials with Ángulo de flexión a 90° of 1.0 °/t	O	EN 573-3, EN 485

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape
Calor específico	20.0 °C	893.0 J/(kg·K) Show Material materials with Calor específico of 893.0 J/(kg·K)	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Rod
Coeficiente de dilatación térmica	20 °C	2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K	O	EN 573-3, EN 1396, EN 485, EN 546
	100 °C	2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K	O	EN 573-3, EN 1396, EN 485, EN 546
Conductividad térmica		160.0 - 190.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 - 190.0 W/(m·K)	O	EN 573-3, EN 1396, EN 485, EN 546
	20.0 °C	200.0 W/(m·K) Show Material materials with Conductividad térmica of 200.0 W/(m·K)	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Rod
Temperatura de fusión		630.0 - 654.0 °C Show Material materials with Temperatura de fusión of 630.0 - 654.0 °C	O	EN 573-3, EN 1396, EN 485, EN 546

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica		23000000.0 - 25000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 25000000.0 S/m	O	EN 573-3, EN 1396, EN 485, EN 546
	20.0 °C	28000000.0 S/m Show Material materials with Conductividad eléctrica of 28000000.0 S/m	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Rod
Resistividad eléctrica		4e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 4e-08 - 4.35e-08 Ω·m	O	EN 573-3, EN 1396, EN 485, EN 546

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.3 % Show Material materials with Cobre of 0.3 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546	Sheet, Flat, Rod
Cromo	0.1 % Show Material materials with Cromo of 0.1 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546	Sheet, Flat, Rod
Hierro	0.7 % Show Material materials with Hierro of 0.7 %	O	DIN 1725-1, EN 573-3, EN 573-4	Sheet, Flat, Rod
	0.70 % Show Material materials with Hierro of 0.70 %	O	EN 573-3, EN 1396, EN 485, EN 546
Magnesio	0.2 - 0.6 % Show Material materials with Magnesio of 0.2 - 0.6 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546	Sheet, Flat, Rod
Manganeso	1.0 - 1.5 % Show Material materials with Manganeso of 1.0 - 1.5 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546	Sheet, Flat, Rod
Silicona	0.6 % Show Material materials with Silicona of 0.6 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546	Sheet, Flat, Rod
Titanio	0.1 % Show Material materials with Titanio of 0.1 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546	Sheet, Flat, Rod
Zinc	0.25 % Show Material materials with Zinc of 0.25 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 1396, EN 485, EN 546	Sheet, Flat, Rod

Technological properties

Property

Anodizing

decorative: sufficient, Protective: very good

Corrosion properties

Seawater: very good, weathering: very good

Workability

Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) very good (O) / acceptable (H12)