EN 573-3 Grade 3.0526 O

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlMn1Mg1 has similar properties like AlMn1, however it reaches higher strength (to F 26). It has also relatively high strength in the soft condition, but it is well cold fomrable. The alloy belongs to the nature-hard aluminum materials. A strength increase can be achieved, not by a purposeful heat treatment only by cold forming. It is very well warm and cold transformable and is suitable to the deep-drawing (no lappet formation). The alloy is very corrosion and sea water-steadily. The main field of application, the packing, determines the kind of semi-finished material standardized according to DIN 1788 and DIN 1745 (sheet metal and strip). Application: In the packing (DIN 59606) for cans (dose lower parts, abgestreckte doses), breaking covers and catches of all kinds. In the building industry for roofings (usually profile boards), claddings as well as for roll shutter and roll gates.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³	O	EN 573-3, EN 485
	20.0 °C	2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³	O	DIN 1725-1, EN 573-3, EN 573-4	Flat

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 3000 Series Aluminium
Dureza Brinell		45.0 [-] Show Material materials with Dureza Brinell of 45.0 [-]	O	EN 573-3, EN 485
	20.0 °C	45.0 [-] Show Material materials with Dureza Brinell of 45.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Elongación	-196.0 °C	38.0 % Show Material materials with Elongación of 38.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	-80.0 °C	30.0 % Show Material materials with Elongación of 30.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	-28.0 °C	26.0 % Show Material materials with Elongación of 26.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
		13.0 % Show Material materials with Elongación of 13.0 %	O	EN 573-3, EN 485		A50
		14.0 % Show Material materials with Elongación of 14.0 %	O	EN 573-3, EN 485		A100
		14.0 % Show Material materials with Elongación of 14.0 %	O	EN 573-3, EN 485		A50
		15.0 % Show Material materials with Elongación of 15.0 %	O	EN 573-3, EN 485		A50
		16.0 % Show Material materials with Elongación of 16.0 %	O	EN 573-3, EN 485		A50
	20.0 °C	7.0 % Show Material materials with Elongación of 7.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	10.0 % Show Material materials with Elongación of 10.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	13.0 % Show Material materials with Elongación of 13.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A100
	20.0 °C	15.0 % Show Material materials with Elongación of 15.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat	A10
	20.0 °C	18.0 % Show Material materials with Elongación of 18.0 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	20.0 °C	25.0 % Show Material materials with Elongación of 25.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	100.0 °C	25.0 % Show Material materials with Elongación of 25.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	150.0 °C	35.0 % Show Material materials with Elongación of 35.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	200.0 °C	55.0 % Show Material materials with Elongación of 55.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	260.0 °C	70.0 % Show Material materials with Elongación of 70.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	315.0 °C	80.0 % Show Material materials with Elongación of 80.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
	370.0 °C	90.0 % Show Material materials with Elongación of 90.0 %	O	DIN 1725-1, EN 573-3, EN 573-4
Módulo de cizallamiento	20.0 °C	25.0 - 27.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 - 27.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Módulo elástico		69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa	O	EN 573-3, EN 485
		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	O	EN 573-3, EN 485
	20.0 °C	65.0 - 71.0 GPa Show Material materials with Módulo elástico of 65.0 - 71.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 3000 Series Aluminium
Resistencia a la tracción	-196.0 °C	290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	-80.0 °C	190.0 MPa Show Material materials with Resistencia a la tracción of 190.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	-28.0 °C	180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	20.0 °C	155.0 - 200.0 MPa Show Material materials with Resistencia a la tracción of 155.0 - 200.0 MPa	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	20.0 °C	180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	100.0 °C	180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	150.0 °C	150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	200.0 °C	95.0 MPa Show Material materials with Resistencia a la tracción of 95.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	260.0 °C	70.0 MPa Show Material materials with Resistencia a la tracción of 70.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	315.0 °C	50.0 MPa Show Material materials with Resistencia a la tracción of 50.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
	370.0 °C	35.0 MPa Show Material materials with Resistencia a la tracción of 35.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4
Ángulo de flexión a 180°		0.5 °/t Show Material materials with Ángulo de flexión a 180° of 0.5 °/t	O	EN 573-3, EN 485
		1.0 °/t Show Material materials with Ángulo de flexión a 180° of 1.0 °/t	O	EN 573-3, EN 485
Ángulo de flexión a 90°		1.0 °/t Show Material materials with Ángulo de flexión a 90° of 1.0 °/t	O	EN 573-3, EN 485
		2.0 °/t Show Material materials with Ángulo de flexión a 90° of 2.0 °/t	O	EN 573-3, EN 485

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape
Calor específico		893.0 J/(kg·K) Show Material materials with Calor específico of 893.0 J/(kg·K)	O	EN 573-3, EN 485
	20.0 °C	893.0 J/(kg·K) Show Material materials with Calor específico of 893.0 J/(kg·K)	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Coeficiente de dilatación térmica	-50 °C	2.1499999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1499999999999997e-05 1/K	O	EN 573-3, EN 485
	-50.0 °C	2.15e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.15e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	20 °C	2.1499999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1499999999999997e-05 1/K	O	EN 573-3, EN 485
	20 °C	2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K	O	EN 573-3, EN 485
	20 °C	2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K	O	EN 573-3, EN 485
	20 °C	2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	20 °C	2.51e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.51e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	100 °C	2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K	O	EN 573-3, EN 485
	100.0 °C	2.32e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.32e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	100 °C	2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K	O	EN 573-3, EN 485
	200 °C	2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	200.0 °C	2.41e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.41e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	300 °C	2.51e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.51e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
	300.0 °C	2.51e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.51e-05 1/K	O	EN 573-3, EN 485, DIN 1725-1, EN 573-4	Flat
Conductividad térmica		160.0 - 180.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 - 180.0 W/(m·K)	O	EN 573-3, EN 485
		163 W/(m·K) Show Material materials with Conductividad térmica of 163 W/(m·K)	O	EN 573-3, EN 485
	20.0 °C	160.0 - 190.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 - 190.0 W/(m·K)	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Temperatura de fusión		629.0 - 654.0 °C Show Material materials with Temperatura de fusión of 629.0 - 654.0 °C	O	EN 573-3, EN 485
		630.0 - 655.0 °C Show Material materials with Temperatura de fusión of 630.0 - 655.0 °C	O	EN 573-3, EN 485

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica		23000000.0 - 25000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 25000000.0 S/m	O	EN 573-3, EN 485
		24000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 S/m	O	EN 573-3, EN 485
	20.0 °C	20000000.0 - 24000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 - 24000000.0 S/m	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
Resistividad eléctrica		4e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 4e-08 - 4.35e-08 Ω·m	O	EN 573-3, EN 485
		4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.17e-08 Ω·m	O	EN 573-3, EN 485

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.25 % Show Material materials with Cobre of 0.25 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Hierro	0.7 % Show Material materials with Hierro of 0.7 %	O	DIN 1725-1, EN 573-3, EN 573-4	Flat
	0.70 % Show Material materials with Hierro of 0.70 %	O	EN 573-3, EN 485
Magnesio	0.8 - 1.3 % Show Material materials with Magnesio of 0.8 - 1.3 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Manganeso	1.0 - 1.5 % Show Material materials with Manganeso of 1.0 - 1.5 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Silicona	0.3 % Show Material materials with Silicona of 0.3 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat
Zinc	0.25 % Show Material materials with Zinc of 0.25 %	O	DIN 1725-1, EN 573-3, EN 573-4, EN 485	Flat

Technological properties

Property

Anodizing

decorative: sufficient, Protective: very good

Corrosion properties

Seawater: very good, weathering: very good

Workability

Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) very good (H14) / acceptable (H12)