DIN 1725-1 Grade 3.3537 H24

Want to keep this datasheet? Save it now in your required format

Description

With AlMg2,7Mn a press effect arises with products of extruding, which causes noticeable strength increases in press direction. This feature is likewise a consequence of the Mn-addition like the increase of the heat resistance. AlMg2,7Mn can be used due to the relatively good physical properties also for statically loaded constructions. The alloy is characterised by a good corrosion resistance. It is sea water steady and steady against saline atmosphere. With the Mg content the strength increases, while the cold forming capacity decreases. The material is nature hard, i.e. that only by a cold forming, however not by a purposeful heat treatment a strength increase can be attained. The splinter-giving workability and the weldability are improved with increasing Mg content. The alloy Al2,7Mn is standardised as semi-finished material only as sheet metal or strip, thickness > 0,35 mm (DIN 1745) Application: In the apparatus engineering for receivers according to VdTUEV-Werkstoffblaetter (cold carburetor, liquid air separation), for tanks for very low-temperatures and for temperatures to 250 °C. In the automobile engineering for silo and tank trucks, dump truck hollows, buses, cool and air conditioning systems, in the building industry for carrying constructions and for thermal insulation as well as in food industry for commercial devices.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Usos

Sistemas de fluido

Almacenamiento de fluidos

Recipientes de presión

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³	H24	EN 573-3, EN 485
	20.0 °C	2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Bending Fatigue Strength		130.0 MPa Show Material materials with Bending Fatigue Strength of 130.0 MPa	H24	EN 573-3, EN 485
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 5000 Series Aluminium
Dureza Brinell		80.0 [-] Show Material materials with Dureza Brinell of 80.0 [-]	H24	EN 573-3, EN 485
	20.0 °C	85.0 [-] Show Material materials with Dureza Brinell of 85.0 [-]	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
Elongación		4.0 % Show Material materials with Elongación of 4.0 %	H24	EN 573-3, EN 485		A50
		5.0 % Show Material materials with Elongación of 5.0 %	H24	EN 573-3, EN 485		A50
		6.0 % Show Material materials with Elongación of 6.0 %	H24	EN 573-3, EN 485		A50
		7.0 % Show Material materials with Elongación of 7.0 %	H24	EN 573-3, EN 485		A50
		7.0 % Show Material materials with Elongación of 7.0 %	H24	EN 573-3, EN 485		A100
		8.0 % Show Material materials with Elongación of 8.0 %	H24	EN 573-3, EN 485		A50
	20.0 °C	7.0 % Show Material materials with Elongación of 7.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
	20.0 °C	9.0 % Show Material materials with Elongación of 9.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
Módulo de cizallamiento		26.5 GPa Show Material materials with Módulo de cizallamiento of 26.5 GPa	H24	EN 573-3, EN 485
	20.0 °C	27.0 GPa Show Material materials with Módulo de cizallamiento of 27.0 GPa	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
Módulo elástico		70.5 GPa Show Material materials with Módulo elástico of 70.5 GPa	H24	EN 573-3, EN 485
	20.0 °C	72.0 GPa Show Material materials with Módulo elástico of 72.0 GPa	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Resistencia a la tracción	20.0 °C	270.0 - 325.0 MPa Show Material materials with Resistencia a la tracción of 270.0 - 325.0 MPa	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4, VdTÜV WB 386	Sheet
Ángulo de flexión a 180°		2.5 °/t Show Material materials with Ángulo de flexión a 180° of 2.5 °/t	H24	EN 573-3, EN 485
		3.0 °/t Show Material materials with Ángulo de flexión a 180° of 3.0 °/t	H24	EN 573-3, EN 485
Ángulo de flexión a 90°		1.0 °/t Show Material materials with Ángulo de flexión a 90° of 1.0 °/t	H24	EN 573-3, EN 485
		2.0 °/t Show Material materials with Ángulo de flexión a 90° of 2.0 °/t	H24	EN 573-3, EN 485
		2.5 °/t Show Material materials with Ángulo de flexión a 90° of 2.5 °/t	H24	EN 573-3, EN 485
		3.0 °/t Show Material materials with Ángulo de flexión a 90° of 3.0 °/t	H24	EN 573-3, EN 485
		4.0 °/t Show Material materials with Ángulo de flexión a 90° of 4.0 °/t	H24	EN 573-3, EN 485

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico		900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K)	H24	EN 573-3, EN 485
	20.0 °C	900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K)	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
Coeficiente de dilatación térmica	-50 °C	2.1899999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1899999999999997e-05 1/K	H24	EN 573-3, EN 485
	-50.0 °C	2.19e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.19e-05 1/K	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
	20 °C	2.1899999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1899999999999997e-05 1/K	H24	EN 573-3, EN 485
	20 °C	2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K	H24	EN 573-3, EN 485
	20 °C	2.46e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.46e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4, VdTÜV WB 386	Sheet
	20 °C	2.56e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.56e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4, VdTÜV WB 386	Sheet
	100 °C	2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K	H24	EN 573-3, EN 485
	100.0 °C	2.37e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.37e-05 1/K	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
	200 °C	2.46e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.46e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4, VdTÜV WB 386	Sheet
	200.0 °C	2.46e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.46e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4, VdTÜV WB 386	Sheet
	300 °C	2.56e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.56e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4, VdTÜV WB 386	Sheet
	300.0 °C	2.56e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.56e-05 1/K	H24	EN 573-3, EN 485, DIN 1725-1, EN 573-4, VdTÜV WB 386	Sheet
Conductividad térmica		130.0 - 150.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 - 150.0 W/(m·K)	H24	EN 573-3, EN 485
	20.0 °C	150.0 W/(m·K) Show Material materials with Conductividad térmica of 150.0 W/(m·K)	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
Temperatura de fusión		602.0 - 646.0 °C Show Material materials with Temperatura de fusión of 602.0 - 646.0 °C	H24	EN 573-3, EN 485
Temperatura máx. de funcionamiento		150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C				Typical for Wrought 5000 Series Aluminium

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica		19000000.0 - 21000000.0 S/m Show Material materials with Conductividad eléctrica of 19000000.0 - 21000000.0 S/m	H24	EN 573-3, EN 485
	20.0 °C	21000000.0 S/m Show Material materials with Conductividad eléctrica of 21000000.0 S/m	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
Resistividad eléctrica		4.76e-08 - 5.26e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.76e-08 - 5.26e-08 Ω·m	H24	EN 573-3, EN 485

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.1 % Show Material materials with Cobre of 0.1 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386, EN 485	Sheet
Cromo	0.05 - 0.2 % Show Material materials with Cromo of 0.05 - 0.2 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386, EN 485	Sheet
Hierro	0.4 % Show Material materials with Hierro of 0.4 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386	Sheet
	0.40 % Show Material materials with Hierro of 0.40 %	H24	EN 573-3, EN 485
Magnesio	2.4 - 3.0 % Show Material materials with Magnesio of 2.4 - 3.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386, EN 485	Sheet
Manganeso	0.5 - 1.0 % Show Material materials with Manganeso of 0.5 - 1.0 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386, EN 485	Sheet
Silicona	0.25 % Show Material materials with Silicona of 0.25 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386, EN 485	Sheet
Titanio	0.2 % Show Material materials with Titanio of 0.2 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386, EN 485	Sheet
Zinc	0.25 % Show Material materials with Zinc of 0.25 %	H24	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 386, EN 485	Sheet

Technological properties

Property
Anodizing	decorative: sufficient, Protective: good
Brazing	hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor
Corrosion properties	Seawater: very good, weathering: very good
Workability	Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (H12)