Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.66 g/cm³ Show Material materials with Densidad of 2.66 g/cm³ | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Dureza Brinell | 65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-] | H112 | EN 573-3, EN 586 | |
73.0 [-] Show Material materials with Dureza Brinell of 73.0 [-] | H112 | EN 573-3, EN 485 | ||
75.0 [-] Show Material materials with Dureza Brinell of 75.0 [-] | H112 | EN 573-3, EN 485 | ||
Módulo de cizallamiento | 26.8 GPa Show Material materials with Módulo de cizallamiento of 26.8 GPa | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | |
Módulo elástico | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Resistencia a la tracción | 260.0 MPa Show Material materials with Resistencia a la tracción of 260.0 MPa | H112 | EN 573-3, EN 485, EN 586 | |
270.0 MPa Show Material materials with Resistencia a la tracción of 270.0 MPa | H112 | EN 573-3, EN 485, EN 603, EN 755 | ||
275.0 MPa Show Material materials with Resistencia a la tracción of 275.0 MPa | H112 | EN 573-3, EN 485 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
Coeficiente de dilatación térmica | -50 °C | 2.23e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.23e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | |
20 °C | 2.23e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.23e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
20 °C | 2.42e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.42e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
20 °C | 2.4999999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4999999999999998e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
20 °C | 2.6e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.6e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
100 °C | 2.42e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.42e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
200 °C | 2.4999999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4999999999999998e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
300 °C | 2.6e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.6e-05 1/K | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
Conductividad térmica | 110.0 - 140.0 W/(m·K) Show Material materials with Conductividad térmica of 110.0 - 140.0 W/(m·K) | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
Temperatura de fusión | 574.0 - 638.0 °C Show Material materials with Temperatura de fusión of 574.0 - 638.0 °C | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 | ||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 16000000.0 - 19000000.0 S/m Show Material materials with Conductividad eléctrica of 16000000.0 - 19000000.0 S/m | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Resistividad eléctrica | 5.26e-08 - 6.25e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.26e-08 - 6.25e-08 Ω·m | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 0.1 % Show Material materials with Cobre of 0.1 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Cromo | 0.05 - 0.25 % Show Material materials with Cromo of 0.05 - 0.25 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Magnesio | 4.0 - 4.9 % Show Material materials with Magnesio of 4.0 - 4.9 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Manganeso | 0.4 - 1.0 % Show Material materials with Manganeso of 0.4 - 1.0 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H112 | EN 573-3, EN 485, EN 586, EN 603, EN 755 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: sufficient, Protective: good | |
| Brazing | hard brazing (with flux/ without flux): poor / poor, friction soldering: acceptable, soft brazing with flux: poor | |
| Corrosion properties | Seawater: very good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O) | |