EN 573-3 Grade 3.3206 T6

Want to keep this datasheet? Save it now in your required format

Description

This cold and hot hardenable material reaches mechanical strength from 200 to 250 MPa with A5-elongation at break of approx. 10 %. In the warm and cold-hardened state this alloy is only limited ductile, in the soft material condition however well. Weldability, corrosion resistance and anodising of this material are good. Due to the special suitability of this alloy for the extrusion those are present lot of profile cross-sectional shapes for application in static loading case in the automobile construction or in the building industry. The company Erbsloeh Aluminum leads under evenly this material number among other things the trade name AlMgSi0,3. It pay attention that only two further trade names (6030 and 466) of this company to this designation are to be assigned. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperatures hot ageing: 4 to 16 h at 155 to 190 °C. Application: Window, doors, window walls, front plates, roller shutter, roll gates, bearing constructions, heat exchanger (gilled pipes), commercial motor vehicle superstructures, machine tables, metal goods, food industry, equipment of rail-mounted vehicles (stroke sun roofs, railroad car doors), optics, reflectors, operating sectors of hydraulic/pneumatics in mechanical engineering, trunk superstructures in the boat and shipbuilding, sail masts, road signs, trim in the automobile engineering, shower cubicles, fences and partitions, pipings in compressed gas tanks, camping furniture.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	T6	EN 573-3, EN 1301, EN 754, EN 755
	20.0 °C	2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Forging, Wire

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Bending Fatigue Strength		80.0 MPa Show Material materials with Bending Fatigue Strength of 80.0 MPa	T6	EN 573-3, EN 1301, EN 754, EN 755
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Dureza Brinell	20.0 °C	65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-]	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Forging, Wire
Elongación		6.0 % Show Material materials with Elongación of 6.0 %	T6	EN 573-3, EN 755		A50
		8.0 % Show Material materials with Elongación of 8.0 %	T6	EN 573-3, EN 755		A100
		10.0 % Show Material materials with Elongación of 10.0 %	T6	EN 573-3, EN 754		A50
		12.0 % Show Material materials with Elongación of 12.0 %	T6	EN 573-3, EN 754		A100
	20.0 °C	5.0 % Show Material materials with Elongación of 5.0 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire	A100
	20.0 °C	9.0 % Show Material materials with Elongación of 9.0 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire	A10
	20.0 °C	12.0 % Show Material materials with Elongación of 12.0 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Forging
Módulo de cizallamiento		26.1 GPa Show Material materials with Módulo de cizallamiento of 26.1 GPa	T6	EN 573-3, EN 1301, EN 754, EN 755
	20.0 °C	25.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 GPa	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Forging, Wire
Módulo elástico		69.5 GPa Show Material materials with Módulo elástico of 69.5 GPa	T6	EN 573-3, EN 1301, EN 754, EN 755
	20.0 °C	67.0 GPa Show Material materials with Módulo elástico of 67.0 GPa	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Forging, Wire
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Resistencia a la tracción		170.0 MPa Show Material materials with Resistencia a la tracción of 170.0 MPa	T6	EN 573-3, EN 755
		190.0 MPa Show Material materials with Resistencia a la tracción of 190.0 MPa	T6	EN 573-3, EN 755
		210.0 MPa Show Material materials with Resistencia a la tracción of 210.0 MPa	T6	EN 573-3, EN 1301
		215.0 MPa Show Material materials with Resistencia a la tracción of 215.0 MPa	T6	EN 573-3, EN 754
	20.0 °C	215.0 MPa Show Material materials with Resistencia a la tracción of 215.0 MPa	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Forging, Wire
Resistencia al cizallamiento	20.0 °C	140.0 MPa Show Material materials with Resistencia al cizallamiento of 140.0 MPa	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape
Calor específico		898.0 J/(kg·K) Show Material materials with Calor específico of 898.0 J/(kg·K)	T6	EN 573-3, EN 1301, EN 754, EN 755
Coeficiente de dilatación térmica	-50 °C	2.18e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.18e-05 1/K	T6	EN 573-3, EN 1301, EN 754, EN 755
	20 °C	2.18e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.18e-05 1/K	T6	EN 573-3, EN 1301, EN 754, EN 755
	20 °C	2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K	T6	EN 573-3, EN 1301, EN 754, EN 755
	20 °C	2.45e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.45e-05 1/K	T6	EN 573-3, EN 1301, EN 754, EN 755
	20 °C	2.56e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.56e-05 1/K	T6	EN 573-3, EN 1301, EN 754, EN 755
	100 °C	2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K	T6	EN 573-3, EN 1301, EN 754, EN 755
	200 °C	2.45e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.45e-05 1/K	T6	EN 573-3, EN 1301, EN 754, EN 755
	300 °C	2.56e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.56e-05 1/K	T6	EN 573-3, EN 1301, EN 754, EN 755
Conductividad térmica		200.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 200.0 - 220.0 W/(m·K)	T6	EN 573-3, EN 1301, EN 754, EN 755
	20.0 °C	220.0 W/(m·K) Show Material materials with Conductividad térmica of 220.0 W/(m·K)	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Forging, Wire
Temperatura de fusión		585.0 - 650.0 °C Show Material materials with Temperatura de fusión of 585.0 - 650.0 °C	T6	EN 573-3, EN 1301, EN 754, EN 755

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica		34000000.0 - 38000000.0 S/m Show Material materials with Conductividad eléctrica of 34000000.0 - 38000000.0 S/m	T6	EN 573-3, EN 1301, EN 754, EN 755
	20.0 °C	30000000.0 - 32000000.0 S/m Show Material materials with Conductividad eléctrica of 30000000.0 - 32000000.0 S/m	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Forging, Wire
Resistividad eléctrica		2.63e-08 - 2.94e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.63e-08 - 2.94e-08 Ω·m	T6	EN 573-3, EN 1301, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.1 % Show Material materials with Cobre of 0.1 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4, EN 1301, EN 754, EN 755	Forging, Wire
Cromo	0.05 % Show Material materials with Cromo of 0.05 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4, EN 1301, EN 754, EN 755	Forging, Wire
Hierro	0.1 - 0.3 % Show Material materials with Hierro of 0.1 - 0.3 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4, EN 1301, EN 754, EN 755	Forging, Wire
Magnesio	0.35 - 0.6 % Show Material materials with Magnesio of 0.35 - 0.6 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4, EN 1301, EN 754, EN 755	Forging, Wire
Manganeso	0.1 % Show Material materials with Manganeso of 0.1 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4, EN 1301, EN 754, EN 755	Forging, Wire
Silicona	0.3 - 0.6 % Show Material materials with Silicona of 0.3 - 0.6 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4, EN 1301, EN 754, EN 755	Forging, Wire
Titanio	0.1 % Show Material materials with Titanio of 0.1 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4, EN 1301, EN 754, EN 755	Forging, Wire
Zinc	0.15 % Show Material materials with Zinc of 0.15 %	T6	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4, EN 1301, EN 754, EN 755	Forging, Wire

Technological properties

Property
Anodizing	decorative: EQ: sehr gut, Protective: very good
Brazing	hard brazing (with flux/ without flux): very good / good, friction soldering: very good, soft brazing with flux: good
Corrosion properties	Seawater: good, weathering: very good
Workability	Bending / Spinning (cold): acceptable (T3, T4) / -, Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) - / good (O)

Looking for suppliers of this material? Click to see 6 supplier of EN 573-3 Grade 3.3206 T6 on Matmatch