Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H111 | EN 573-3, EN 754, EN 755 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Módulo de cizallamiento | 26.3 GPa Show Material materials with Módulo de cizallamiento of 26.3 GPa | H111 | EN 573-3, EN 754, EN 755 | |
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | H111 | EN 573-3, EN 754, EN 755 | |
70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | H111 | EN 573-3, EN 754, EN 755 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Resistencia a la tracción | 150.0 Show Material materials with Resistencia a la tracción of 150.0 | H111 | EN 573-3, EN 754, EN 755 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 887.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | H111 | EN 573-3, EN 754, EN 755 | |
20 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | H111 | EN 573-3, EN 754, EN 755 | ||
100 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | H111 | EN 573-3, EN 754, EN 755 | ||
100 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | H111 | EN 573-3, EN 754, EN 755 | ||
Conductividad térmica | 155.0 - 180.0 W/(m·K) Show Material materials with Conductividad térmica of 155.0 - 180.0 W/(m·K) | H111 | EN 573-3, EN 754, EN 755 | ||
170.0 - 200.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 - 200.0 W/(m·K) | H111 | EN 573-3, EN 754, EN 755 | |||
Temperatura de fusión | 580.0 - 640.0 °C Show Material materials with Temperatura de fusión of 580.0 - 640.0 °C | H111 | EN 573-3, EN 754, EN 755 | ||
580.0 - 650.0 °C Show Material materials with Temperatura de fusión of 580.0 - 650.0 °C | H111 | EN 573-3, EN 754, EN 755 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 22000000.0 - 30000000.0 S/m Show Material materials with Conductividad eléctrica of 22000000.0 - 30000000.0 S/m | H111 | EN 573-3, EN 754, EN 755 |
23000000.0 - 27000000.0 S/m Show Material materials with Conductividad eléctrica of 23000000.0 - 27000000.0 S/m | H111 | EN 573-3, EN 754, EN 755 | |
Resistividad eléctrica | 3.33e-08 - 4.55e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.33e-08 - 4.55e-08 Ω·m | H111 | EN 573-3, EN 754, EN 755 |
3.7e-08 - 4.35e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.7e-08 - 4.35e-08 Ω·m | H111 | EN 573-3, EN 754, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 0.15 - 0.4 % Show Material materials with Cobre of 0.15 - 0.4 % | H111 | EN 573-3, EN 754, EN 755 |
Cromo | 0.04 - 0.35 % Show Material materials with Cromo of 0.04 - 0.35 % | H111 | EN 573-3, EN 754, EN 755 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | H111 | EN 573-3, EN 754, EN 755 |
Magnesio | 0.8 - 1.2 % Show Material materials with Magnesio of 0.8 - 1.2 % | H111 | EN 573-3, EN 754, EN 755 |
Manganeso | 0.15 % Show Material materials with Manganeso of 0.15 % | H111 | EN 573-3, EN 754, EN 755 |
Silicona | 0.4 - 0.8 % Show Material materials with Silicona of 0.4 - 0.8 % | H111 | EN 573-3, EN 754, EN 755 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | H111 | EN 573-3, EN 754, EN 755 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H111 | EN 573-3, EN 754, EN 755 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): good / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
| Corrosion properties | Seawater: good to acceptable, weathering: good | |
| Workability | Bending / Spinning (cold): acceptable (T3, T4) / good (O), Impact extrusion (cold): good (O), Deep drawing / upsetting (Condition) good (O) / good (O) | |