Propiedades
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Densidad | 2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | ||
20.0 °C | 2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4 | Plate, Rod, Sheet, Forging, Wire |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 150.0 MPa Show Material materials with Bending Fatigue Strength of 150.0 MPa | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | |||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Dureza Brinell | 104.0 [-] Show Material materials with Dureza Brinell of 104.0 [-] | T6 | EN 573-3, EN 485 | |||
119.0 [-] Show Material materials with Dureza Brinell of 119.0 [-] | T6 | EN 573-3, EN 485 | ||||
135.0 [-] Show Material materials with Dureza Brinell of 135.0 [-] | T6 | EN 573-3, EN 485, EN 586 | ||||
144.0 [-] Show Material materials with Dureza Brinell of 144.0 [-] | T6 | EN 573-3, EN 485 | ||||
147.0 [-] Show Material materials with Dureza Brinell of 147.0 [-] | T6 | EN 573-3, EN 485 | ||||
155.0 [-] Show Material materials with Dureza Brinell of 155.0 [-] | T6 | EN 573-3, EN 485 | ||||
157.0 [-] Show Material materials with Dureza Brinell of 157.0 [-] | T6 | EN 573-3, EN 485 | ||||
158.0 [-] Show Material materials with Dureza Brinell of 158.0 [-] | T6 | EN 573-3, EN 485 | ||||
160.0 [-] Show Material materials with Dureza Brinell of 160.0 [-] | T6 | EN 573-3, EN 485 | ||||
161.0 [-] Show Material materials with Dureza Brinell of 161.0 [-] | T6 | EN 573-3, EN 485 | ||||
163.0 [-] Show Material materials with Dureza Brinell of 163.0 [-] | T6 | EN 573-3, EN 485 | ||||
20.0 °C | 130.0 [-] Show Material materials with Dureza Brinell of 130.0 [-] | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 135.0 [-] Show Material materials with Dureza Brinell of 135.0 [-] | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 140.0 [-] Show Material materials with Dureza Brinell of 140.0 [-] | T6 | WL 3.4364-1, DIN 1725-1 | Sheet, Plate, Rod | Transverse | |
20.0 °C | 140.0 [-] Show Material materials with Dureza Brinell of 140.0 [-] | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Wire, Rod | ||
Elongación | 1.0 % Show Material materials with Elongación of 1.0 % | T6 | EN 573-3, EN 485 | A100 | ||
2.0 % Show Material materials with Elongación of 2.0 % | T6 | EN 573-3, EN 485 | A100 | |||
3.0 % Show Material materials with Elongación of 3.0 % | T6 | EN 573-3, EN 485 | A100 | |||
4.0 % Show Material materials with Elongación of 4.0 % | T6 | EN 573-3, EN 485, EN 586 | A100 | |||
4.0 % Show Material materials with Elongación of 4.0 % | T6 | EN 573-3, EN 755 | A50 | |||
5.0 % Show Material materials with Elongación of 5.0 % | T6 | EN 573-3, EN 485, EN 755 | A100 | |||
5.0 % Show Material materials with Elongación of 5.0 % | T6 | EN 573-3, EN 755 | A50 | |||
6.0 % Show Material materials with Elongación of 6.0 % | T6 | EN 573-3, EN 485, EN 755 | A100 | |||
6.0 % Show Material materials with Elongación of 6.0 % | T6 | EN 573-3, EN 485, EN 754, EN 755 | A50 | |||
7.0 % Show Material materials with Elongación of 7.0 % | T6 | EN 573-3, EN 754, EN 755 | A100 | |||
7.0 % Show Material materials with Elongación of 7.0 % | T6 | EN 573-3, EN 485 | A50 | |||
8.0 % Show Material materials with Elongación of 8.0 % | T6 | EN 573-3, EN 755 | A100 | |||
8.0 % Show Material materials with Elongación of 8.0 % | T6 | EN 573-3, EN 485 | A50 | |||
10.0 % Show Material materials with Elongación of 10.0 % | T6 | EN 573-3, EN 1301 | ||||
10.0 % Show Material materials with Elongación of 10.0 % | T6 | EN 573-3, EN 1592 | A100 | |||
20.0 °C | 2.0 % Show Material materials with Elongación of 2.0 % | T6 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 2.0 % Show Material materials with Elongación of 2.0 % | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Wire | A100 | |
20.0 °C | 3.0 % Show Material materials with Elongación of 3.0 % | T6 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 3.0 % Show Material materials with Elongación of 3.0 % | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 4.0 % Show Material materials with Elongación of 4.0 % | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 5.0 % Show Material materials with Elongación of 5.0 % | T6 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 6.0 % Show Material materials with Elongación of 6.0 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4 | Rod, Forging | ||
20.0 °C | 6.0 % Show Material materials with Elongación of 6.0 % | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Wire | A10 | |
20.0 °C | 7.0 % Show Material materials with Elongación of 7.0 % | T6 | WL 3.4364-1, DIN 1725-1 | Rod | ||
20.0 °C | 8.0 % Show Material materials with Elongación of 8.0 % | T6 | WL 3.4364-1, DIN 1725-1 | Sheet, Plate | Transverse | |
Módulo de cizallamiento | 27.1 GPa Show Material materials with Módulo de cizallamiento of 27.1 GPa | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | |||
20.0 °C | 25.0 - 27.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 - 27.0 GPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging, Wire | ||
Módulo de compresibilidad | 20.0 °C | 72.5 GPa Show Material materials with Módulo de compresibilidad of 72.5 GPa | T6 | WL 3.4364-1, DIN 1725-1 | Plate, Rod, Sheet | |
Módulo elástico | 72.0 GPa Show Material materials with Módulo elástico of 72.0 GPa | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | |||
20.0 °C | 70.0 - 73.0 GPa Show Material materials with Módulo elástico of 70.0 - 73.0 GPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging, Wire | ||
20.0 °C | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | T6 | WL 3.4364-1, DIN 1725-1 | Plate, Rod, Sheet | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||||
Resistencia a la tracción | 360.0 MPa Show Material materials with Resistencia a la tracción of 360.0 MPa | T6 | EN 573-3, EN 485 | |||
410.0 MPa Show Material materials with Resistencia a la tracción of 410.0 MPa | T6 | EN 573-3, EN 485 | ||||
460.0 MPa Show Material materials with Resistencia a la tracción of 460.0 MPa | T6 | EN 573-3, EN 485 | ||||
470.0 MPa Show Material materials with Resistencia a la tracción of 470.0 MPa | T6 | EN 573-3, EN 586, EN 755 | ||||
480.0 MPa Show Material materials with Resistencia a la tracción of 480.0 MPa | T6 | EN 573-3, EN 586 | ||||
490.0 MPa Show Material materials with Resistencia a la tracción of 490.0 MPa | T6 | EN 573-3, EN 485 | ||||
495.0 MPa Show Material materials with Resistencia a la tracción of 495.0 MPa | T6 | EN 573-3, EN 485 | ||||
510.0 MPa Show Material materials with Resistencia a la tracción of 510.0 MPa | T6 | EN 573-3, EN 1301 | ||||
525.0 MPa Show Material materials with Resistencia a la tracción of 525.0 MPa | T6 | EN 573-3, EN 485 | ||||
530.0 MPa Show Material materials with Resistencia a la tracción of 530.0 MPa | T6 | EN 573-3, EN 1592, EN 485, EN 755 | ||||
540.0 MPa Show Material materials with Resistencia a la tracción of 540.0 MPa | T6 | EN 573-3, EN 485, EN 754, EN 755 | ||||
545.0 MPa Show Material materials with Resistencia a la tracción of 545.0 MPa | T6 | EN 573-3, EN 485 | ||||
560.0 MPa Show Material materials with Resistencia a la tracción of 560.0 MPa | T6 | EN 573-3, EN 755 | ||||
20.0 °C | 440.0 MPa Show Material materials with Resistencia a la tracción of 440.0 MPa | T6 | WL 3.4364-1, DIN 1725-1 | Rod | Transverse | |
20.0 °C | 440.0 MPa Show Material materials with Resistencia a la tracción of 440.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 450.0 MPa Show Material materials with Resistencia a la tracción of 450.0 MPa | T6 | WL 3.4364-1, DIN 1725-1 | Rod | Transverse | |
20.0 °C | 450.0 MPa Show Material materials with Resistencia a la tracción of 450.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 460.0 MPa Show Material materials with Resistencia a la tracción of 460.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 470.0 MPa Show Material materials with Resistencia a la tracción of 470.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 480.0 MPa Show Material materials with Resistencia a la tracción of 480.0 MPa | T6 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 480.0 MPa Show Material materials with Resistencia a la tracción of 480.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 490.0 MPa Show Material materials with Resistencia a la tracción of 490.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 500.0 MPa Show Material materials with Resistencia a la tracción of 500.0 MPa | T6 | WL 3.4364-1, DIN 1725-1 | Plate | Transverse | |
20.0 °C | 500.0 MPa Show Material materials with Resistencia a la tracción of 500.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 510.0 MPa Show Material materials with Resistencia a la tracción of 510.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Wire | ||
20.0 °C | 530.0 MPa Show Material materials with Resistencia a la tracción of 530.0 MPa | T6 | WL 3.4364-1, DIN 1725-1 | Sheet, Plate | Transverse | |
20.0 °C | 540.0 MPa Show Material materials with Resistencia a la tracción of 540.0 MPa | T6 | WL 3.4364-1, DIN 1725-1 | Rod | ||
20.0 °C | 550.0 MPa Show Material materials with Resistencia a la tracción of 550.0 MPa | T6 | WL 3.4364-1, DIN 1725-1 | Rod | ||
Ángulo de flexión a 90° | 4.5 °/t Show Material materials with Ángulo de flexión a 90° of 4.5 °/t | T6 | EN 573-3, EN 485 | |||
5.5 °/t Show Material materials with Ángulo de flexión a 90° of 5.5 °/t | T6 | EN 573-3, EN 485 | ||||
6.5 °/t Show Material materials with Ángulo de flexión a 90° of 6.5 °/t | T6 | EN 573-3, EN 485 | ||||
8.0 °/t Show Material materials with Ángulo de flexión a 90° of 8.0 °/t | T6 | EN 573-3, EN 485 | ||||
12.0 °/t Show Material materials with Ángulo de flexión a 90° of 12.0 °/t | T6 | EN 573-3, EN 485 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Calor específico | 862.0 J/(kg·K) Show Material materials with Calor específico of 862.0 J/(kg·K) | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | ||
20.0 °C | 862.0 J/(kg·K) Show Material materials with Calor específico of 862.0 J/(kg·K) | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging, Wire | |
Coeficiente de dilatación térmica | -50 °C | 2.16e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.16e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire |
-50.0 °C | 2.16e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.16e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire | |
20 °C | 2.16e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.16e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire | |
20 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | ||
20 °C | 2.43e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.43e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire | |
20 °C | 2.52e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.52e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3399999999999996e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | ||
100.0 °C | 2.34e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.34e-05 1/K | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging, Wire | |
200 °C | 2.43e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.43e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire | |
200.0 °C | 2.43e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.43e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire | |
300 °C | 2.52e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.52e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire | |
300.0 °C | 2.52e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.52e-05 1/K | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755, DIN 1725-1, EN 573-4, WL 3.4364-1 | Forging, Wire | |
Conductividad térmica | 20.0 °C | 130.0 - 160.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 - 160.0 W/(m·K) | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Forging, Wire |
Temperatura de fusión | 480.0 - 640.0 °C Show Material materials with Temperatura de fusión of 480.0 - 640.0 °C | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 |
Eléctrico
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Conductividad eléctrica | 20.0 °C | 19000000.0 - 23000000.0 S/m Show Material materials with Conductividad eléctrica of 19000000.0 - 23000000.0 S/m | T6 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Forging, Wire |
Resistividad eléctrica | 4.35e-08 - 5.26e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.35e-08 - 5.26e-08 Ω·m | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Cobre | 1.2 - 2.0 % Show Material materials with Cobre of 1.2 - 2.0 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Plate, Rod, Sheet, Forging, Wire |
Cromo | 0.18 - 0.28 % Show Material materials with Cromo of 0.18 - 0.28 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Plate, Rod, Sheet, Forging, Wire |
Hierro | 0.5 % Show Material materials with Hierro of 0.5 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4 | Plate, Rod, Sheet, Forging, Wire |
0.50 % Show Material materials with Hierro of 0.50 % | T6 | EN 573-3, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | ||
Magnesio | 2.1 - 2.9 % Show Material materials with Magnesio of 2.1 - 2.9 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Plate, Rod, Sheet, Forging, Wire |
Manganeso | 0.3 % Show Material materials with Manganeso of 0.3 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Plate, Rod, Sheet, Forging, Wire |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Plate, Rod, Sheet, Forging, Wire |
Titanio | 0.2 % Show Material materials with Titanio of 0.2 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Plate, Rod, Sheet, Forging, Wire |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T6 | WL 3.4364-1, DIN 1725-1, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 586, EN 754, EN 755 | Plate, Rod, Sheet, Forging, Wire |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not suitable, Protective: acceptable | |
| Brazing | hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: not suitable, soft brazing with flux: not suitable | |
| Corrosion properties | Seawater: sufficient to poor, weathering: sufficient to poor | |
| Workability | Bending / Spinning (cold): sufficient (O) / not suitable, Impact extrusion (cold): not suitable, Deep drawing / upsetting (Condition) not suitable / not suitable | |