General
Property | Value | Condition | Related Standards |
---|---|---|---|
Densidad | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H44 | EN 573-3, EN 1396 |
Mecánica
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 35.0 MPa Show Material materials with Bending Fatigue Strength of 35.0 MPa | H44 | EN 573-3, EN 1396 | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Módulo de cizallamiento | 25.9 GPa Show Material materials with Módulo de cizallamiento of 25.9 GPa | H44 | EN 573-3, EN 1396 | |
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | H44 | EN 573-3, EN 1396 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Resistencia a la tracción | 100.0 - 145.0 MPa Show Material materials with Resistencia a la tracción of 100.0 - 145.0 MPa | H44 | EN 573-3, EN 1396 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Calor específico | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | H44 | EN 573-3, EN 1396 | |
Coeficiente de dilatación térmica | -50 °C | 2.17e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.17e-05 1/K | H44 | EN 573-3, EN 1396 |
20 °C | 2.17e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.17e-05 1/K | H44 | EN 573-3, EN 1396 | |
20 °C | 2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K | H44 | EN 573-3, EN 1396 | |
20 °C | 2.4399999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4399999999999997e-05 1/K | H44 | EN 573-3, EN 1396 | |
20 °C | 2.5399999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.5399999999999997e-05 1/K | H44 | EN 573-3, EN 1396 | |
100 °C | 2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K | H44 | EN 573-3, EN 1396 | |
200 °C | 2.4399999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4399999999999997e-05 1/K | H44 | EN 573-3, EN 1396 | |
300 °C | 2.5399999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.5399999999999997e-05 1/K | H44 | EN 573-3, EN 1396 | |
Conductividad térmica | 210.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 210.0 - 220.0 W/(m·K) | H44 | EN 573-3, EN 1396 | |
Temperatura de fusión | 646.0 - 657.0 °C Show Material materials with Temperatura de fusión of 646.0 - 657.0 °C | H44 | EN 573-3, EN 1396 |
Eléctrico
Property | Value | Condition | Related Standards |
---|---|---|---|
Conductividad eléctrica | 34000000.0 - 36000000.0 S/m Show Material materials with Conductividad eléctrica of 34000000.0 - 36000000.0 S/m | H44 | EN 573-3, EN 1396 |
Resistividad eléctrica | 2.78e-08 - 2.94e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.78e-08 - 2.94e-08 Ω·m | H44 | EN 573-3, EN 1396 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 99.5 % Show Material materials with Aluminio of 99.5 % | H44 | EN 573-3, EN 1396 |
Cobre | 0.05 % Show Material materials with Cobre of 0.05 % | H44 | EN 573-3, EN 1396 |
Hierro | 0.40 % Show Material materials with Hierro of 0.40 % | H44 | EN 573-3, EN 1396 |
Magnesio | 0.05 % Show Material materials with Magnesio of 0.05 % | H44 | EN 573-3, EN 1396 |
Manganeso | 0.05 % Show Material materials with Manganeso of 0.05 % | H44 | EN 573-3, EN 1396 |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | H44 | EN 573-3, EN 1396 |
Titanio | 0.05 % Show Material materials with Titanio of 0.05 % | H44 | EN 573-3, EN 1396 |
Zinc | 0.07 % Show Material materials with Zinc of 0.07 % | H44 | EN 573-3, EN 1396 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: gut (EQ: sehr gut), Protective: very good | |
Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
Corrosion properties | Seawater: acceptable, weathering: good | |
Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12) |