DIN 1712-3 Grade 3.0257 H14

Want to keep this datasheet? Save it now in your required format

Description

Pure aluminium Electrical conductivity alloy according to DIN, ensured by the German electrotechnical commission for electro-technology with, also in accordance to DIN 40 501 part of 1 to part of 4. This material has a very good electrical and good thermal conductivity, however only relatively low mechanical strength. Forming capacity and chemical as well as weather proofness are very good. Application: Roll bond, z-bond, wiring loom-change with particularly high requirements.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	H14	EN 573-3, EN 755
	20.0 °C	2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire, Rod, Tube

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 1000 Series Aluminium
Dureza Brinell		33.0 [-] Show Material materials with Dureza Brinell of 33.0 [-]	H14	EN 573-3, EN 755
	20.0 °C	28.0 - 38.0 [-] Show Material materials with Dureza Brinell of 28.0 - 38.0 [-]	H14	DIN 1712-3, EN 573-3, EN 573-4	Rod, Tube
Elongación		5.0 % Show Material materials with Elongación of 5.0 %	H14	EN 573-3, EN 755		A50
		6.0 % Show Material materials with Elongación of 6.0 %	H14	EN 573-3, EN 755		A100
	20.0 °C	2.0 % Show Material materials with Elongación of 2.0 %	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire	A200
	20.0 °C	3.0 % Show Material materials with Elongación of 3.0 %	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire	A100
	20.0 °C	5.0 % Show Material materials with Elongación of 5.0 %	H14	DIN 1712-3, EN 573-3, EN 573-4	Tube	A10
	20.0 °C	6.0 % Show Material materials with Elongación of 6.0 %	H14	DIN 1712-3, EN 573-3, EN 573-4	Rod	A10
	20.0 °C	6.0 % Show Material materials with Elongación of 6.0 %	H14	DIN 1712-3, EN 573-3, EN 573-4	Tube
	20.0 °C	7.0 % Show Material materials with Elongación of 7.0 %	H14	DIN 1712-3, EN 573-3, EN 573-4	Rod
Módulo de cizallamiento	20.0 °C	25.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 25.0 - 26.5 GPa	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire, Rod, Tube
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	H14	EN 573-3, EN 755
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 1000 Series Aluminium
Resistencia a la tracción		100.0 - 135.0 MPa Show Material materials with Resistencia a la tracción of 100.0 - 135.0 MPa	H14	EN 573-3, EN 755
	20.0 °C	90.0 - 130.0 MPa Show Material materials with Resistencia a la tracción of 90.0 - 130.0 MPa	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire
	20.0 °C	100.0 - 140.0 MPa Show Material materials with Resistencia a la tracción of 100.0 - 140.0 MPa	H14	DIN 1712-3, EN 573-3, EN 573-4, EN 755	Rod, Tube

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape
Calor específico	20.0 °C	921.0 J/(kg·K) Show Material materials with Calor específico of 921.0 J/(kg·K)	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire, Rod, Tube
Coeficiente de dilatación térmica	20 °C	2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K	H14	EN 573-3, EN 755
	100 °C	2.35e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.35e-05 1/K	H14	EN 573-3, EN 755
Conductividad térmica		230 W/(m·K) Show Material materials with Conductividad térmica of 230 W/(m·K)	H14	EN 573-3, EN 755
	20.0 °C	230.0 W/(m·K) Show Material materials with Conductividad térmica of 230.0 W/(m·K)	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire, Rod, Tube
Temperatura de fusión		658.0 °C Show Material materials with Temperatura de fusión of 658.0 °C	H14	EN 573-3, EN 755

Eléctrico

Property	Value	Condition	Related Standards
Conductividad eléctrica	34500000.0 - 35500000.0 S/m Show Material materials with Conductividad eléctrica of 34500000.0 - 35500000.0 S/m	H14	EN 573-3, EN 755
Resistividad eléctrica	2.82e-08 - 2.9e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.82e-08 - 2.9e-08 Ω·m	H14	EN 573-3, EN 755

Chemical properties

Property	Value	Condition	Related Standards	Shape
Aluminio	99.5 % Show Material materials with Aluminio of 99.5 %	H14	EN 573-3, EN 755
Cobre	0.02 % Show Material materials with Cobre of 0.02 %	H14	DIN 1712-3, EN 573-3, EN 573-4, EN 755	Wire, Rod, Tube
Hierro	0.4 % Show Material materials with Hierro of 0.4 %	H14	DIN 1712-3, EN 573-3, EN 573-4	Wire, Rod, Tube
	0.40 % Show Material materials with Hierro of 0.40 %	H14	EN 573-3, EN 755
Magnesio	0.05 % Show Material materials with Magnesio of 0.05 %	H14	DIN 1712-3, EN 573-3, EN 573-4, EN 755	Wire, Rod, Tube
Silicona	0.25 % Show Material materials with Silicona of 0.25 %	H14	DIN 1712-3, EN 573-3, EN 573-4, EN 755	Wire, Rod, Tube
Zinc	0.05 % Show Material materials with Zinc of 0.05 %	H14	DIN 1712-3, EN 573-3, EN 573-4, EN 755	Wire, Rod, Tube

Technological properties

Property

Brazing

Excellent

Workability

Excellent workability.