Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | T652 | AA Standards, ASTM B247 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Módulo de cizallamiento | 26.0 - 27.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Módulo elástico | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T652 | AA Standards, ASTM B247 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Resistencia a la tracción | 395.0 MPa Show Material materials with Resistencia a la tracción of 395.0 MPa | T652 | AA Standards, ASTM B247 | |
400.0 MPa Show Material materials with Resistencia a la tracción of 400.0 MPa | T652 | AA Standards, ASTM B247 | ||
405.0 MPa Show Material materials with Resistencia a la tracción of 405.0 MPa | T652 | AA Standards, ASTM B247 | ||
415.0 MPa Show Material materials with Resistencia a la tracción of 415.0 MPa | T652 | AA Standards, ASTM B247 | ||
420.0 MPa Show Material materials with Resistencia a la tracción of 420.0 MPa | T652 | AA Standards, ASTM B247 | ||
425.0 MPa Show Material materials with Resistencia a la tracción of 425.0 MPa | T652 | AA Standards, ASTM B247 | ||
435.0 MPa Show Material materials with Resistencia a la tracción of 435.0 MPa | T652 | AA Standards, ASTM B247 | ||
440.0 MPa Show Material materials with Resistencia a la tracción of 440.0 MPa | T652 | AA Standards, ASTM B247 | ||
450.0 MPa Show Material materials with Resistencia a la tracción of 450.0 MPa | T652 | AA Standards, ASTM B247 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 816.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T652 | AA Standards, ASTM B247 | |
100 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T652 | AA Standards, ASTM B247 | ||
Conductividad térmica | 134.0 - 193.0 W/(m·K) Show Material materials with Conductividad térmica of 134.0 - 193.0 W/(m·K) | T652 | AA Standards, ASTM B247 | ||
Temperatura de fusión | 505.0 - 635.0 °C Show Material materials with Temperatura de fusión of 505.0 - 635.0 °C | T652 | AA Standards, ASTM B247 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 20000000.0 - 29000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 - 29000000.0 S/m | T652 | AA Standards, ASTM B247 |
Resistividad eléctrica | 3.45e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.45e-08 - 5e-08 Ω·m | T652 | AA Standards, ASTM B247 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 3.9 - 5.0 % Show Material materials with Cobre of 3.9 - 5.0 % | T652 | AA Standards, ASTM B247 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T652 | AA Standards, ASTM B247 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | T652 | AA Standards, ASTM B247 |
Magnesio | 0.2 - 0.8 % Show Material materials with Magnesio of 0.2 - 0.8 % | T652 | AA Standards, ASTM B247 |
Manganeso | 0.4 - 1.2 % Show Material materials with Manganeso of 0.4 - 1.2 % | T652 | AA Standards, ASTM B247 |
Silicona | 0.5 - 1.2 % Show Material materials with Silicona of 0.5 - 1.2 % | T652 | AA Standards, ASTM B247 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T652 | AA Standards, ASTM B247 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T652 | AA Standards, ASTM B247 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511) | |