General
Property | Temperature | Value |
---|---|---|
Densidad | 20.0 °C | 8.8 g/cm³ Show Material materials with Densidad of 8.8 g/cm³ |
Medidas
Property | Value |
---|---|
Dimensions | Durchmesser |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Brinell | 20.0 °C | 50 - 75 [-] Show Material materials with Dureza Brinell of 50 - 75 [-] |
Dureza Vickers | 20.0 °C | 55 - 80 [-] Show Material materials with Dureza Vickers of 55 - 80 [-] |
Elongación | 20.0 °C | 35 % Show Material materials with Elongación of 35 % |
Elongation A100 | 20.0 °C | 25 % Show Material materials with Elongation A100 of 25 % |
Límite elástico Rp 0,2 | 20.0 °C | 90 MPa Show Material materials with Límite elástico Rp 0,2 of 90 MPa |
Módulo elástico | 20.0 °C | 143 GPa Show Material materials with Módulo elástico of 143 GPa |
Resistencia a la tracción | 20.0 °C | 240 MPa Show Material materials with Resistencia a la tracción of 240 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 20.0 °C | 1.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6E-5 1/K |
100.0 °C | 1.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6E-5 1/K | |
Conductividad térmica | 20.0 °C | 75 - 126 W/(m·K) Show Material materials with Conductividad térmica of 75 - 126 W/(m·K) |
Temperatura de fusión | 1050 - 1070 °C Show Material materials with Temperatura de fusión of 1050 - 1070 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 20.0 °C | 1.10E+7 - 2.40E+7 S/m Show Material materials with Conductividad eléctrica of 1.10E+7 - 2.40E+7 S/m |
Resistividad eléctrica | 20.0 °C | 4.17E-8 - 9.09E-8 Ω·m Show Material materials with Resistividad eléctrica of 4.17E-8 - 9.09E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Hierro | 0.2 % Show Material materials with Hierro of 0.2 % |
Manganeso | 0.1 % Show Material materials with Manganeso of 0.1 % |
Níquel | 1 - 1.6 % Show Material materials with Níquel of 1 - 1.6 % |
Otro | Rest Cu, total 0.3 |
Plomo | 0.02 % Show Material materials with Plomo of 0.02 % |
Silicona | 0.4 - 0.7 % Show Material materials with Silicona of 0.4 - 0.7 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : good to medium, soft brazing: good | |
Workability | Cold forming degree between anneals: max. 75 % (lösungsgeglüht) |