Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.9 g/cm³ Show Material materials with Densidad of 8.9 g/cm³ |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Vickers | 23.0 °C | 90 [-] Show Material materials with Dureza Vickers of 90 [-] |
Elongación | 23.0 °C | 25 % Show Material materials with Elongación of 25 % |
Límite elástico Rp 0,2 | 23.0 °C | 120 MPa Show Material materials with Límite elástico Rp 0,2 of 120 MPa |
Módulo elástico | 23.0 °C | 130 GPa Show Material materials with Módulo elástico of 130 GPa |
Resistencia a la tracción | 23.0 °C | 300 MPa Show Material materials with Resistencia a la tracción of 300 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 375 - 398 J/(kg·K) Show Material materials with Calor específico of 375 - 398 J/(kg·K) | Typical for Wrought Copper Nickel Grade |
Coeficiente de dilatación térmica | 20.0 °C | 1.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.7E-5 1/K | |
100.0 °C | 1.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.7E-5 1/K | ||
Conductividad térmica | 23.0 °C | 46 W/(m·K) Show Material materials with Conductividad térmica of 46 W/(m·K) | |
Temperatura de fusión | 1100 - 1145 °C Show Material materials with Temperatura de fusión of 1100 - 1145 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 23.0 °C | 5.30E+6 S/m Show Material materials with Conductividad eléctrica of 5.30E+6 S/m |
Resistividad eléctrica | 23.0 °C | 1.89E-7 Ω·m Show Material materials with Resistividad eléctrica of 1.89E-7 Ω·m |
Chemical properties
Property | Value |
---|---|
Azufre | 0.05 % Show Material materials with Azufre of 0.05 % |
Carbono | 0.05 % Show Material materials with Carbono of 0.05 % |
Cobalto | 0.1 % Show Material materials with Cobalto of 0.1 % |
Estaño | 0.3 % Show Material materials with Estaño of 0.3 % |
Fósforo | 0.02 % Show Material materials with Fósforo of 0.02 % |
Hierro | 1 - 2 % Show Material materials with Hierro of 1 - 2 % |
Manganeso | 0.5 - 1 % Show Material materials with Manganeso of 0.5 - 1 % |
Níquel | 9 - 11 % Show Material materials with Níquel of 9 - 11 % |
Otro | Rest Cu, total 0.2 |
Plomo | 0.02 % Show Material materials with Plomo of 0.02 % |
Zinc | 0.5 % Show Material materials with Zinc of 0.5 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : very good, soft brazing: very good | |
Workability | Cold forming degree between anneals: max. 80 %, general (condition): very good |