General
Property | Temperature | Value |
---|---|---|
Densidad | 20.0 °C | 8.4 g/cm³ Show Material materials with Densidad of 8.4 g/cm³ |
Medidas
Property | Value |
---|---|
Dimensions | Dicke |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Vickers | 20.0 °C | 55 - 95 [-] Show Material materials with Dureza Vickers of 55 - 95 [-] |
Elongación | 20.0 °C | 48 % Show Material materials with Elongación of 48 % |
Elongación A50 | 20.0 °C | 38 % Show Material materials with Elongación A50 of 38 % |
Límite elástico Rp 0,2 | 20.0 °C | 180 MPa Show Material materials with Límite elástico Rp 0,2 of 180 MPa |
Módulo elástico | 20.0 °C | 110 GPa Show Material materials with Módulo elástico of 110 GPa |
Resistencia a la tracción | 20.0 °C | 300 - 370 MPa Show Material materials with Resistencia a la tracción of 300 - 370 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 20.0 °C | 2.02E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.02E-5 1/K |
100.0 °C | 2.02E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.02E-5 1/K | |
Conductividad térmica | 20.0 °C | 121 W/(m·K) Show Material materials with Conductividad térmica of 121 W/(m·K) |
Temperatura de fusión | 902 - 920 °C Show Material materials with Temperatura de fusión of 902 - 920 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 20.0 °C | 1.50E+7 S/m Show Material materials with Conductividad eléctrica of 1.50E+7 S/m |
Resistividad eléctrica | 20.0 °C | 6.67E-8 Ω·m Show Material materials with Resistividad eléctrica of 6.67E-8 Ω·m |
Chemical properties
Property | Value |
---|---|
Aluminio | 0.02 % Show Material materials with Aluminio of 0.02 % |
Cobre | 63.5 - 65.5 % Show Material materials with Cobre of 63.5 - 65.5 % |
Estaño | 0.1 % Show Material materials with Estaño of 0.1 % |
Hierro | 0.05 % Show Material materials with Hierro of 0.05 % |
Níquel | 0.3 % Show Material materials with Níquel of 0.3 % |
Otro | Rest Zn, total 0.1 |
Plomo | 0.05 % Show Material materials with Plomo of 0.05 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : very good, soft brazing: very good | |
Workability | Cold forming degree between anneals: max. 65 %, general (condition): very good |