Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.705 g/cm³ Show Material materials with Densidad of 2.705 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 20.0 MPa Show Material materials with Bending Fatigue Strength of 20.0 MPa | O | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Dureza Brinell | 19.0 [-] Show Material materials with Dureza Brinell of 19.0 [-] | O | AA Standards | |
Módulo de cizallamiento | 25.9 GPa Show Material materials with Módulo de cizallamiento of 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Resistencia a la tracción | 55.0 - 95.0 MPa Show Material materials with Resistencia a la tracción of 55.0 - 95.0 MPa | O | AA Standards, ASTM B209 | |
55.0 MPa Show Material materials with Resistencia a la tracción of 55.0 MPa | O | AA Standards, ASTM B211 | ||
60.0 - 95.0 MPa Show Material materials with Resistencia a la tracción of 60.0 - 95.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
70.0 MPa Show Material materials with Resistencia a la tracción of 70.0 MPa | O | AA Standards |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 900.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
100 °C | 2.36e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
Conductividad térmica | 230.0 - 234.0 W/(m·K) Show Material materials with Conductividad térmica of 230.0 - 234.0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
Temperatura de fusión | 645.0 - 655.0 °C Show Material materials with Temperatura de fusión of 645.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 35000000.0 - 36000000.0 S/m Show Material materials with Conductividad eléctrica of 35000000.0 - 36000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Resistividad eléctrica | 2.78e-08 - 2.86e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.78e-08 - 2.86e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 99.6 % Show Material materials with Aluminio of 99.6 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Cobre | 0.05 % Show Material materials with Cobre of 0.05 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Hierro | 0.35 % Show Material materials with Hierro of 0.35 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Magnesio | 0.03 % Show Material materials with Magnesio of 0.03 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Manganeso | 0.03 % Show Material materials with Manganeso of 0.03 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Silicona | 0.25 % Show Material materials with Silicona of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Titanio | 0.03 % Show Material materials with Titanio of 0.03 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Vanadio | 0.05 % Show Material materials with Vanadio of 0.05 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) | |