Property | Value | Condition | Related Standards |
---|---|---|---|
Densidad | 2.72 g/cm³ Show Material materials with Densidad of 2.72 g/cm³ | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Mecánica
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | O | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Dureza Brinell | 45.0 [-] Show Material materials with Dureza Brinell of 45.0 [-] | O | AA Standards | |
Módulo de cizallamiento | 25.0 - 26.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Resistencia a la tracción | 150.0 - 200.0 MPa Show Material materials with Resistencia a la tracción of 150.0 - 200.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
160.0 - 200.0 MPa Show Material materials with Resistencia a la tracción of 160.0 - 200.0 MPa | O | AA Standards, ASTM B221 | ||
180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa | O | AA Standards |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Calor específico | 893.0 - 920.0 J/(kg·K) Show Material materials with Calor específico of 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
Conductividad térmica | 163 W/(m·K) Show Material materials with Conductividad térmica of 163 W/(m·K) | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
Temperatura de fusión | 630.0 - 655.0 °C Show Material materials with Temperatura de fusión of 630.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Eléctrico
Property | Value | Condition | Related Standards |
---|---|---|---|
Conductividad eléctrica | 24000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 S/m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Resistividad eléctrica | 4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.17e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Cobre | 0.25 % Show Material materials with Cobre of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Magnesio | 0.8 - 1.3 % Show Material materials with Magnesio of 0.8 - 1.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Manganeso | 1.0 - 1.5 % Show Material materials with Manganeso of 1.0 - 1.5 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Silicona | 0.3 % Show Material materials with Silicona of 0.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Technological properties
Property | ||
---|---|---|
Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) |