General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.26 g/cm³ Show Supplier Material materials with Densidad of 8.26 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Brinell (HBW) | 23.0 °C | 380 [-] Show Supplier Material materials with Dureza Brinell (HBW) of 380 [-] | HBW 10/3000 |
Dureza Rockwell C | 23.0 °C | 40 [-] Show Supplier Material materials with Dureza Rockwell C of 40 [-] | |
Elongación A5 | 23.0 °C | 4 % Show Supplier Material materials with Elongación A5 of 4 % | |
Límite elástico Rp0.5 | 23.0 °C | 1000 MPa Show Supplier Material materials with Límite elástico Rp0.5 of 1000 MPa | |
Módulo elástico | 23.0 °C | 131 GPa Show Supplier Material materials with Módulo elástico of 131 GPa | |
Resistencia a la tracción | 23.0 °C | 1250 MPa Show Supplier Material materials with Resistencia a la tracción of 1250 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 23.0 °C | 380 J/(kg·K) Show Supplier Material materials with Calor específico of 380 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75E-5 1/K |
Conductividad térmica | 20.0 °C | 106 W/(m·K) Show Supplier Material materials with Conductividad térmica of 106 W/(m·K) |
100.0 °C | 130 W/(m·K) Show Supplier Material materials with Conductividad térmica of 130 W/(m·K) | |
200.0 °C | 145 W/(m·K) Show Supplier Material materials with Conductividad térmica of 145 W/(m·K) | |
300.0 °C | 157 W/(m·K) Show Supplier Material materials with Conductividad térmica of 157 W/(m·K) | |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 23.0 °C | 1.28E+7 S/m Show Supplier Material materials with Conductividad eléctrica of 1.28E+7 S/m |
Specific Electrical conductivity | 22 % IACS Show Supplier Material materials with Specific Electrical conductivity of 22 % IACS |
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | 2.1247 is used wherever good wear resistance or high mechanical properties are desired coupled with a good electrical or thermal conductivity, such as: Flash butt welding and butt welding, Parts for electrical components, in the plastic mould industry is sometimes used as chill plates and inserts in the moulds, cooling pins and neck rings or bottom plates for blow moulds of plastic bottles. |