Propiedades
General
| Property | Temperature | Value |
|---|---|---|
Densidad | 23.0 °C | 6.93 g/cm³ Show Supplier Material materials with Densidad of 6.93 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dureza Brinell (HBW) | 23.0 °C | 364 [-] Show Supplier Material materials with Dureza Brinell (HBW) of 364 [-] | HBW 10/3000 |
Dureza Rockwell C | 23.0 °C | 38 [-] Show Supplier Material materials with Dureza Rockwell C of 38 [-] | |
Límite elástico a la compresión, 0,1% | 23.0 °C | 689 MPa Show Supplier Material materials with Límite elástico a la compresión, 0,1% of 689 MPa | |
Módulo elástico | 23.0 °C | 110 GPa Show Supplier Material materials with Módulo elástico of 110 GPa | |
Resistencia a la compresión | 23.0 °C | 1551 MPa Show Supplier Material materials with Resistencia a la compresión of 1551 MPa |
Aplicaciones térmicas
| Property | Temperature | Value |
|---|---|---|
Calor específico | 23.0 °C | 420 J/(kg·K) Show Supplier Material materials with Calor específico of 420 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 1.62E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.62E-5 1/K |
Conductividad térmica | 23.0 °C | 33 W/(m·K) Show Supplier Material materials with Conductividad térmica of 33 W/(m·K) |
Eléctrico
| Property | Temperature | Value |
|---|---|---|
Conductividad eléctrica | 23.0 °C | 4.00E+6 S/m Show Supplier Material materials with Conductividad eléctrica of 4.00E+6 S/m |
Specific Electrical conductivity | 8 % IACS Show Supplier Material materials with Specific Electrical conductivity of 8 % IACS |
Chemical properties
| Property | Value |
|---|---|
Cobre | Balance |
Technological properties
| Property | ||
|---|---|---|
| Application areas | The phenomenal success of this alloy led to its use as forming rolls, bending and wiping blocks and it is considered the standard material in this field of applications. Due to its inherent friction properties, this alloy has an excellent behaviour in any wear application where high compression loads are present. | |