General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.26 g/cm³ Show Supplier Material materials with Densidad of 8.26 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Brinell (HBW) | 23.0 °C | 340 [-] Show Supplier Material materials with Dureza Brinell (HBW) of 340 [-] | HBW 10/3000 |
Dureza Rockwell C | 23.0 °C | 36 [-] Show Supplier Material materials with Dureza Rockwell C of 36 [-] | |
Elongación A5 | 23.0 °C | 5 % Show Supplier Material materials with Elongación A5 of 5 % | |
Energía de impacto Charpy | 23.0 °C | 1.3 J Show Supplier Material materials with Energía de impacto Charpy of 1.3 J | |
Energía de impacto Izod | 23.0 °C | 2.6 J Show Supplier Material materials with Energía de impacto Izod of 2.6 J | |
Estricción | 23.0 °C | 2.5 % Show Supplier Material materials with Estricción of 2.5 % | |
Límite elástico Rp0.5 | 23.0 °C | 1000 MPa Show Supplier Material materials with Límite elástico Rp0.5 of 1000 MPa | |
Límite proporcional | 23.0 °C | 586 MPa Show Supplier Material materials with Límite proporcional of 586 MPa | |
Límite proporcional en compresión | 23.0 °C | 655 MPa Show Supplier Material materials with Límite proporcional en compresión of 655 MPa | |
Módulo elástico | 23.0 °C | 128 GPa Show Supplier Material materials with Módulo elástico of 128 GPa | |
Resistencia a la compresión | 23.0 °C | 1654 MPa Show Supplier Material materials with Resistencia a la compresión of 1654 MPa | |
Resistencia a la fatiga | 23.0 °C | 330 MPa Show Supplier Material materials with Resistencia a la fatiga of 330 MPa | 100.000.000 cycles |
Resistencia a la tracción | 23.0 °C | 1140 MPa Show Supplier Material materials with Resistencia a la tracción of 1140 MPa | |
Resistencia al cizallamiento | 23.0 °C | 620 MPa Show Supplier Material materials with Resistencia al cizallamiento of 620 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 23.0 °C | 380 J/(kg·K) Show Supplier Material materials with Calor específico of 380 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75E-5 1/K |
Conductividad térmica | 23.0 °C | 106 W/(m·K) Show Supplier Material materials with Conductividad térmica of 106 W/(m·K) |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 23.0 °C | 2.20E+7 S/m Show Supplier Material materials with Conductividad eléctrica of 2.20E+7 S/m |
Specific Electrical conductivity | 22 % IACS Show Supplier Material materials with Specific Electrical conductivity of 22 % IACS |
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | 2.1247 is used wherever good wear resistance or high mechanical properties are desired coupled with a good electrical or thermal conductivity, such as: Flash butt welding and butt welding, Parts for electrical components, in the plastic mould industry is sometimes used as chill plates and inserts in the moulds, cooling pins and neck rings or bottom plates for blow moulds of plastic bottles. |