Propiedades
General
| Property | Temperature | Value |
|---|---|---|
Densidad | 23.0 °C | 7.95 g/cm³ Show Supplier Material materials with Densidad of 7.95 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dureza Brinell (HBW) | 23.0 °C | 163 - 187 [-] Show Supplier Material materials with Dureza Brinell (HBW) of 163 - 187 [-] | HBW 10/3000 |
Dureza Rockwell B | 23.0 °C | 85 - 91 [-] Show Supplier Material materials with Dureza Rockwell B of 85 - 91 [-] | |
Elongación A5 | 23.0 °C | 35 % Show Supplier Material materials with Elongación A5 of 35 % | |
Energía de impacto Charpy | 23.0 °C | 41 - 54 J Show Supplier Material materials with Energía de impacto Charpy of 41 - 54 J | |
Energía de impacto Izod | 23.0 °C | 61 - 75 J Show Supplier Material materials with Energía de impacto Izod of 61 - 75 J | |
Estricción | 23.0 °C | 55 - 63 % Show Supplier Material materials with Estricción of 55 - 63 % | |
Límite elástico Rp0.5 | 23.0 °C | 283 - 386 MPa Show Supplier Material materials with Límite elástico Rp0.5 of 283 - 386 MPa | |
Límite elástico a la compresión, 0,1% | 23.0 °C | 324 MPa Show Supplier Material materials with Límite elástico a la compresión, 0,1% of 324 MPa | |
Límite proporcional en compresión | 23.0 °C | 138 - 179 MPa Show Supplier Material materials with Límite proporcional en compresión of 138 - 179 MPa | |
Módulo elástico | 23.0 °C | 124 GPa Show Supplier Material materials with Módulo elástico of 124 GPa | |
Resistencia a la compresión | 23.0 °C | 862 - 931 MPa Show Supplier Material materials with Resistencia a la compresión of 862 - 931 MPa | |
Resistencia a la tracción | 23.0 °C | 517 - 586 MPa Show Supplier Material materials with Resistencia a la tracción of 517 - 586 MPa | |
Resistencia al cizallamiento | 23.0 °C | 276 - 331 MPa Show Supplier Material materials with Resistencia al cizallamiento of 276 - 331 MPa |
Aplicaciones térmicas
| Property | Temperature | Value |
|---|---|---|
Calor específico | 23.0 °C | 420 J/(kg·K) Show Supplier Material materials with Calor específico of 420 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 1.63E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.63E-5 1/K |
Conductividad térmica | 23.0 °C | 54 W/(m·K) Show Supplier Material materials with Conductividad térmica of 54 W/(m·K) |
Eléctrico
| Property | Temperature | Value |
|---|---|---|
Conductividad eléctrica | 23.0 °C | 7.00E+6 S/m Show Supplier Material materials with Conductividad eléctrica of 7.00E+6 S/m |
Specific Electrical conductivity | 12 % IACS Show Supplier Material materials with Specific Electrical conductivity of 12 % IACS |
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | AMPCO® 8 is used whenever good resistance to corrosion, erosion, abrasion and cavitation-pitting is essential. AMPCO® 8 is ideally suited for pipes, tubes, joints and other pieces used in the process, marine or other similar industries. The extreme hardness of this alloy makes it an ideal bolting material. AMPCO® 8 has excellent bearing characteristics. It is used for bushings, bearings, wear strips and in similar applications where hardness and ductility are essential for uninterrupted operations. | |