Propiedades
General
| Property | Temperature | Value |
|---|---|---|
Densidad | 23.0 °C | 7.45 g/cm³ Show Supplier Material materials with Densidad of 7.45 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dureza Brinell (HBW) | 23.0 °C | 187 - 202 [-] Show Supplier Material materials with Dureza Brinell (HBW) of 187 - 202 [-] | HBW 10/3000 |
Dureza Rockwell B | 23.0 °C | 91 - 94 [-] Show Supplier Material materials with Dureza Rockwell B of 91 - 94 [-] | |
Elongación A5 | 23.0 °C | 12 - 14 % Show Supplier Material materials with Elongación A5 of 12 - 14 % | |
Energía de impacto Charpy | 23.0 °C | 12 - 14 J Show Supplier Material materials with Energía de impacto Charpy of 12 - 14 J | |
Energía de impacto Izod | 23.0 °C | 19 - 22 J Show Supplier Material materials with Energía de impacto Izod of 19 - 22 J | |
Estricción | 23.0 °C | 12 - 14 % Show Supplier Material materials with Estricción of 12 - 14 % | |
Límite elástico Rp0.5 | 23.0 °C | 338 - 379 MPa Show Supplier Material materials with Límite elástico Rp0.5 of 338 - 379 MPa | |
Límite elástico a la compresión, 0,1% | 23.0 °C | 262 MPa Show Supplier Material materials with Límite elástico a la compresión, 0,1% of 262 MPa | |
Límite proporcional en compresión | 23.0 °C | 221 - 248 MPa Show Supplier Material materials with Límite proporcional en compresión of 221 - 248 MPa | |
Módulo elástico | 23.0 °C | 117 GPa Show Supplier Material materials with Módulo elástico of 117 GPa | |
Resistencia a la compresión | 23.0 °C | 980 - 1013 MPa Show Supplier Material materials with Resistencia a la compresión of 980 - 1013 MPa | |
Resistencia a la fatiga | 23.0 °C | 241 - 248 MPa Show Supplier Material materials with Resistencia a la fatiga of 241 - 248 MPa | 100.000.000 cycles |
Resistencia a la tracción | 23.0 °C | 655 - 745 MPa Show Supplier Material materials with Resistencia a la tracción of 655 - 745 MPa | |
Resistencia al cizallamiento | 23.0 °C | 428 - 448 MPa Show Supplier Material materials with Resistencia al cizallamiento of 428 - 448 MPa |
Aplicaciones térmicas
| Property | Temperature | Value |
|---|---|---|
Calor específico | 23.0 °C | 420 J/(kg·K) Show Supplier Material materials with Calor específico of 420 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 1.62E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.62E-5 1/K |
Conductividad térmica | 23.0 °C | 63 W/(m·K) Show Supplier Material materials with Conductividad térmica of 63 W/(m·K) |
Eléctrico
| Property | Temperature | Value |
|---|---|---|
Conductividad eléctrica | 23.0 °C | 7.00E+6 S/m Show Supplier Material materials with Conductividad eléctrica of 7.00E+6 S/m |
Specific Electrical conductivity | 12 % IACS Show Supplier Material materials with Specific Electrical conductivity of 12 % IACS |
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | AMPCO® 18 rod is produced with a good surface finish to commercial tolerances and can be used economically for volume-production applications. AMPCO® 18 is ideally suited where high strength and hardness combined with wear and fatigue resistance are required. Some of the more common applications of this alloy are bushings, bearings, gears, worm wheels, valve seats and guides, hydraulic valve parts, pump rods, guide pin bushings, gibs and slides, etc. | |