Propiedades
General
| Property | Value |
|---|---|
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dureza Brinell | 23.0 °C | 80 [-] Show Supplier Material materials with Dureza Brinell of 80 [-] | BHN (500 kg) 1/4″ deposit |
Elongación | 23.0 °C | 40 % Show Supplier Material materials with Elongación of 40 % | in 2″ (51 mm) |
Resistencia a la tracción | 23.0 °C | 350 MPa Show Supplier Material materials with Resistencia a la tracción of 350 MPa |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Aluminio | 0.01 % Show Supplier Material materials with Aluminio of 0.01 % | max. | |
Cobre | Balance, including silver | ||
Estaño | 1 % Show Supplier Material materials with Estaño of 1 % | max. | |
Hierro | 0.5 % Show Supplier Material materials with Hierro of 0.5 % | max. | |
Manganeso | 1.5 % Show Supplier Material materials with Manganeso of 1.5 % | max. | |
Otro | 0.5 % Show Supplier Material materials with Otro of 0.5 % | max. | |
Plomo | 0.02 % Show Supplier Material materials with Plomo of 0.02 % | max. | |
Silicona | 2.8 - 4 % Show Supplier Material materials with Silicona of 2.8 - 4 % | ||
Zinc | 1 % Show Supplier Material materials with Zinc of 1 % | max. | |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Welding Procedure: With gas metal-arc welding, the weld metal should be deposited in stringer beads, maintaining a small molten pool to avoid overheating the hot short silicon bronze base metal. Use argon gas for shielding and relatively high welding travel speeds. With the gas-tungsten arc welding process, welding is accomplished with dcen current and argon or helium gas shielding. ACHF with argon gas shielding may be used to take advantage of the arc cleaning action. Preheat: Preheat slightly to remove moisture. Interpass temperature should not exceed 150°F (66°C). | |