General
Property | Value | Testing Standard | Comment |
---|---|---|---|
Absorción de agua | 0.02 % Show Supplier Material materials with Absorción de agua of 0.02 % | Sim. to ISO 62 | |
Coefficient of friction | 0.12 [-] Show Supplier Material materials with Coefficient of friction of 0.12 [-] | ASTM D1894 | vs Steel, Kinetic |
0.18 [-] Show Supplier Material materials with Coefficient of friction of 0.18 [-] | ASTM D1894 | vs Steel, Static | |
Densidad | 1.84 - 1.88 g/cm³ Show Supplier Material materials with Densidad of 1.84 - 1.88 g/cm³ | ASTM D792 | |
Índice límite de óxigeno | 44 % Show Supplier Material materials with Índice límite de óxigeno of 44 % | ASTM D2863 |
Mecánica
Property | Temperature | Value | Testing Standard | Condition | Comment |
---|---|---|---|---|---|
Dureza Shore D | 74 - 79 [-] Show Supplier Material materials with Dureza Shore D of 74 - 79 [-] | ASTM D2240 | |||
Elongación | 0 - 20 % Show Supplier Material materials with Elongación of 0 - 20 % | ASTM D638 | |||
Elongation at yield | 0 % Show Supplier Material materials with Elongation at yield of 0 % | ASTM D638 | |||
4 % Show Supplier Material materials with Elongation at yield of 4 % | ASTM D638 | ||||
Impact strength, Charpy notched, ASTM | 23 °C | 40 - 80.1 J/m Show Supplier Material materials with Impact strength, Charpy notched, ASTM of 40 - 80.1 J/m | ASTM D256 | ||
Impact strength, Charpy unnotched, ASTM | 23 °C | 267 - 534 J/m Show Supplier Material materials with Impact strength, Charpy unnotched, ASTM of 267 - 534 J/m | ASTM D256 | ||
Límite elástico | 34.5 - 55.2 MPa Show Supplier Material materials with Límite elástico of 34.5 - 55.2 MPa | ASTM D638 | |||
42 MPa Show Supplier Material materials with Límite elástico of 42 MPa | ISO 527-1/-2 | dry | |||
Módulo de flexión | 5.5 - 6.9 GPa Show Supplier Material materials with Módulo de flexión of 5.5 - 6.9 GPa | ASTM D790 | |||
Módulo elástico | 3.1 - 5.2 GPa Show Supplier Material materials with Módulo elástico of 3.1 - 5.2 GPa | ASTM D638 | |||
Resistencia a la compresión | 138 - 172 MPa Show Supplier Material materials with Resistencia a la compresión of 138 - 172 MPa | ASTM D695 | |||
Resistencia a la flexión | 138 - 207 MPa Show Supplier Material materials with Resistencia a la flexión of 138 - 207 MPa | ASTM D790 | at 5% strain | ||
Resistencia a la tracción | 37.9 - 55.2 MPa Show Supplier Material materials with Resistencia a la tracción of 37.9 - 55.2 MPa | ASTM D638 |
Aplicaciones térmicas
Property | Value | Testing Standard | Condition | Pressure | Comment | ||||
---|---|---|---|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 3.6e-05 - 4.5e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3.6e-05 - 4.5e-05 1/K | ASTM D696 | |||||||
4e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 4e-05 1/K | ISO 11359-1/-2 | dry | |||||||
Temperatura de flexión bajo carga | 110 - 127 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 110 - 127 °C | ASTM D648 | 2 MPa | 248 °F/hr | |||||
120 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 120 °C | ISO 75-1/-2 | dry | 2 MPa | ||||||
132 - 149 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 132 - 149 °C | ASTM D648 | 0.45 MPa | 248 °F/hr | ||||||
Temperatura de fusión | 165 - 170 °C Show Supplier Material materials with Temperatura de fusión of 165 - 170 °C | ASTM D3418 | |||||||
170 °C Show Supplier Material materials with Temperatura de fusión of 170 °C | ISO 11357-1/-3 | dry | 10°C/min | ||||||
Temperatura de transición del vidrio | -40.6 - -38.3 °C Show Supplier Material materials with Temperatura de transición del vidrio of -40.6 - -38.3 °C | ASTM D7028 | |||||||
-40 °C Show Supplier Material materials with Temperatura de transición del vidrio of -40 °C | ISO 11357-1/-2 | dry | 10°C/min | ||||||
Thermal decomposition in air | 375 °C Show Supplier Material materials with Thermal decomposition in air of 375 °C | TGA | 1% wt. loss | ||||||
Thermal decomposition in nitrogen | 410 °C Show Supplier Material materials with Thermal decomposition in nitrogen of 410 °C | TGA | 1% wt. loss | ||||||
Inflamabilidad | At thickness 1.6 mm IEC 60695-11-10: V-0, At thickness 0.8 mm IEC 60695-11-10: V-0 |
Eléctrico
Property | Value | Frequency | Testing Standard | Condition |
---|---|---|---|---|
Constante dieléctrica | 28.8 - 33.5 [-] Show Supplier Material materials with Constante dieléctrica of 28.8 - 33.5 [-] | 1KHz | ASTM D150 | |
33 [-] Show Supplier Material materials with Constante dieléctrica of 33 [-] | 100Hz | IEC 60250 | dry | |
Factor de disipación | 0.06 - 0.08 [-] Show Supplier Material materials with Factor de disipación of 0.06 - 0.08 [-] | 100KHz | ASTM D150 | |
0.061 [-] Show Supplier Material materials with Factor de disipación of 0.061 [-] | 100Hz | IEC 60250 | dry | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | ASTM D257 | 65% RH | |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | IEC 60093 | dry |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Contracción | 0.7 % Show Supplier Material materials with Contracción of 0.7 % | dry | ISO 294-4 | |
0.7 % Show Supplier Material materials with Contracción of 0.7 % | dry | ISO 294-4 | Transverse | |
Density of melt | 1.88 g/cm³ Show Supplier Material materials with Density of melt of 1.88 g/cm³ | |||
Melt viscosity | 800 - 1300 Pa·s Show Supplier Material materials with Melt viscosity of 800 - 1300 Pa·s | ASTM D3835 | ||
Velocidad de flujo de la masa derretida | 5 - 17 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 5 - 17 g/10min | ASTM D1238 | 230°C/3.8kg | |
Velocidad de flujo del volumen derretido | 5.8 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 5.8 cm³/10min | dry | ISO 1133 | 230°C/3.8kg |
Technological properties
Property | ||
---|---|---|
Application areas | Chemical Process Industry | |
Processing methods | Injection Molding: |