Pebax® MV 1074 SA 01 MED

Nombres alternativos y comerciales
TPA

Want to keep this datasheet? Save it now in your required format

Description

Polyether block amide Pebax® MV 1074 SA 01 MED resin is a thermoplastic elastomer made of flexible and hydrophilic polyether and rigid polyamide. Hydrophilic Pebax® MV 1074 SA 01 MED resin is suitable for extrusion or coextrusion and offers excellent high moisture absorption properties in wet environments, enhancing lubricity against bodily tissue.

Pebax® MV 1074 SA 01 MED resin is also an inherently dissipative polymer and can be dry blended or compounded with a polymer matrix to lower the surface resistivity of the final part. This grade offers the highest quality and it is specially designed to meet the stringent requirements of the medical applications such as minimally invasive devices. Upon request, letters regarding USP Class VI compliance can be provided. Refractive index according to an internal method is 1.502.

Los datos sobre este material han sido proporcionados por Arkema Technical Polymers.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Value	Condition	Testing Standard
Densidad	1.07 g/cm³ Show Supplier Material materials with Densidad of 1.07 g/cm³	dry	ISO 1183
Moisture absorption	1.4 % Show Supplier Material materials with Moisture absorption of 1.4 %		Sim. to ISO 62
Índice límite de óxigeno	19 % Show Supplier Material materials with Índice límite de óxigeno of 19 %	dry	ISO 4589-1/-2

Mecánica

Property	Value	Condition	Testing Standard	Comment
Dureza Shore D	40 [-] Show Supplier Material materials with Dureza Shore D of 40 [-]	dry	ISO 7619-1	15 seconds
Elongación	50 % Show Supplier Material materials with Elongación of 50 %	cond., dry	ISO 527-1/-2	min.
	500 % Show Supplier Material materials with Elongación of 500 %	dry	ISO 527-3
	700 % Show Supplier Material materials with Elongación of 700 %	dry	ISO 527-3	Transverse
Módulo elástico	0.08 GPa Show Supplier Material materials with Módulo elástico of 0.08 GPa	cond.	ISO 527-1/-2
	0.097 GPa Show Supplier Material materials with Módulo elástico of 0.097 GPa	dry	ISO 527-1/-2
Resistencia a la tracción	32 MPa Show Supplier Material materials with Resistencia a la tracción of 32 MPa	dry	ISO 527-3
	34 MPa Show Supplier Material materials with Resistencia a la tracción of 34 MPa	dry	ISO 527-3	Transverse
Resistencia al choque, ensayo Charpy entallado	No Break at 23 and -30°C	cond., dry	ISO 179/1eA
Resistencia al choque, ensayo Charpy no entallado	No Break at 23 and -30°C	dry and cond.	ISO 179/1eU

Aplicaciones térmicas

Property	Value	Condition	Testing Standard	Comment
Temperatura de fusión	158 °C Show Supplier Material materials with Temperatura de fusión of 158 °C	dry	ISO 11357-1/-3	10°C/min
Temperatura de transición del vidrio	-40 °C Show Supplier Material materials with Temperatura de transición del vidrio of -40 °C	dry	ISO 11357-1/-2	10°C/min

Eléctrico

Property	Value	Condition	Testing Standard
Rigidez dieléctrica	5 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 5 kV/mm	dry	IEC 60243-1
Surface resistivity	3e+09 Ω/sq Show Supplier Material materials with Surface resistivity of 3e+09 Ω/sq	cond.	IEC 60093
Volume resistivity	2.5e+07 Ω·cm Show Supplier Material materials with Volume resistivity of 2.5e+07 Ω·cm	cond.	IEC 60093
	1.5e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1.5e+11 Ω·cm	dry	IEC 60093

Technological properties

Property

Application areas

Permanent Antistatic Solutions,Antistatic/Breathable,Healthcare-Other,IV Bags,Medical Catheters

Certifications

USP Class VI

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max): 200°C / 240°C / 270°C.

Typical mold temperature: 25–60°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.

Extrusion:

Typical melt temperature (Min / Recommended / Max): 210°C / 220°C / 230°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.

Pebax® MV 1074 SA 01 MED