Propiedades
General
| Property | Value | Testing Standard | Condition |
|---|---|---|---|
Absorción de agua | 3.8 % Show Supplier Material materials with Absorción de agua of 3.8 % | Sim. to ISO 62 | |
Densidad | 1.05 g/cm³ Show Supplier Material materials with Densidad of 1.05 g/cm³ | ISO 1183 | dry |
Moisture absorption | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | Sim. to ISO 62 | |
Índice límite de óxigeno | 26 % Show Supplier Material materials with Índice límite de óxigeno of 26 % | ISO 4589-1/-2 | dry |
Mecánica
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Dureza Shore D | 79 [-] Show Supplier Material materials with Dureza Shore D of 79 [-] | dry | ISO 7619-1 | 15 seconds | |
Elongación | 50 % Show Supplier Material materials with Elongación of 50 % | cond., dry | ISO 527-1/-2 | min. | nominal | |
Elongation at yield | 8 % Show Supplier Material materials with Elongation at yield of 8 % | dry | ISO 527-1/-2 | ||
9 % Show Supplier Material materials with Elongation at yield of 9 % | cond. | ISO 527-1/-2 | |||
Límite elástico | 61 MPa Show Supplier Material materials with Límite elástico of 61 MPa | cond. | ISO 527-1/-2 | ||
Módulo elástico | 2.0 GPa Show Supplier Material materials with Módulo elástico of 2.0 GPa | cond. | ISO 527-1/-2 | ||
2.1 GPa Show Supplier Material materials with Módulo elástico of 2.1 GPa | dry | ISO 527-1/-2 | |||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | cond. | ISO 179/1eA | |
23 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | cond. | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | No Break at -30°C | dry and cond. | ISO 179/1eU |
Aplicaciones térmicas
| Property | Value | Condition | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 7e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 7e-05 1/K | dry | ISO 11359-1/-2 | ||||
Temperatura de reblandecimiento Vicat | 160 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 160 °C | ISO 306 | 50°C/h 50N | ||||
Temperatura de transición del vidrio | 168 °C Show Supplier Material materials with Temperatura de transición del vidrio of 168 °C | dry | ISO 11357-1/-2 | 10°C/min | |||
Inflamabilidad | At thickness 1.6 mm IEC 60695-11-10: HV-2, At thickness 0.8 mm IEC 60695-11-10: HB | ||||||
Eléctrico
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Rigidez dieléctrica | 50 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 50 kV/mm | cond. | IEC 60243-1 |
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | cond. | IEC 60093 |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | cond. | IEC 60093 |
Índice de seguimiento comparativo | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | cond. | IEC 60112 |
Óptico
| Property | Value | Testing Standard |
|---|---|---|
Transmisión lumínica | 91 [-] Show Supplier Material materials with Transmisión lumínica of 91 [-] | ISO 13468-1/2 |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Contracción | 0.7 % Show Supplier Material materials with Contracción of 0.7 % | dry | ISO 294-4 | |
0.7 % Show Supplier Material materials with Contracción of 0.7 % | dry | ISO 294-4 | Transverse | |
Velocidad de flujo del volumen derretido | 2 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 2 cm³/10min | dry | ISO 1133 | 275°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Breathing Masks,Healthcare-Other | |
| Certifications | USP Class VI | |
| Processing methods | Injection Molding: Film Extrusion: | |