General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 6.05 g/cm³ Show Supplier Material materials with Densidad of 6.05 g/cm³ | |
Rugosidad superficial | 3.6 μm Show Supplier Material materials with Rugosidad superficial of 3.6 μm | Rz* |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Vickers | 23.0 °C | 1326 [-] Show Supplier Material materials with Dureza Vickers of 1326 [-] | converted from GPa |
Módulo elástico | 23.0 °C | 210 GPa Show Supplier Material materials with Módulo elástico of 210 GPa | |
Plane-Strain Fracture Toughnes | 23.0 °C | 10.5 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 10.5 MPa·√m | |
Resistencia a la compresión | 23.0 °C | 2400 MPa Show Supplier Material materials with Resistencia a la compresión of 2400 MPa | |
Resistencia a la flexión | 23.0 °C | 1100 MPa Show Supplier Material materials with Resistencia a la flexión of 1100 MPa | 4-point bending flexural test |
Aplicaciones térmicas
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 20.0 °C | 1.00E+9 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.00E+9 Ω·m |
600.0 °C | 10000 Ω·m Show Supplier Material materials with Resistividad eléctrica of 10000 Ω·m | |
Technological properties
Property | ||
---|---|---|
Application areas | Sensor Technology (lambda sensors) for oxygen ion conduction Components that face frequent temperature changes, e.g. draw dies and high-temperature insulating parts In cases where high fracture toughness is required, e.g. for medical instruments | |
Other | *depending on the processing status of the injection molding or pressing tool | |
Processing history | Ceramic Injection Molding (CIM) |