Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.65 g/cm³ Show Supplier Material materials with Densidad of 1.65 g/cm³ | at 230°C |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 2.5 % Show Supplier Material materials with Elongación of 2.5 % | ISO 527-5/Tape, 5mm/min |
Módulo de flexión | 23.0 °C | 31 GPa Show Supplier Material materials with Módulo de flexión of 31 GPa | ISO 14125, 2mm/min |
Módulo elástico | 23.0 °C | 31 GPa Show Supplier Material materials with Módulo elástico of 31 GPa | ISO 527-5/Tape, 1mm/min |
Resistencia a la flexión | 23.0 °C | 750 MPa Show Supplier Material materials with Resistencia a la flexión of 750 MPa | ISO 14125, 2mm/min |
Resistencia a la tracción | 23.0 °C | 700 MPa Show Supplier Material materials with Resistencia a la tracción of 700 MPa | ISO 527-5/Tape, 5 mm/min |
Resistencia al cizallamiento interlaminar | 23.0 °C | 23 MPa Show Supplier Material materials with Resistencia al cizallamiento interlaminar of 23 MPa | ISO 14130, 1mm/min |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.3E-5 1/K | ISO 11359, 23-500°C at 50°C/min |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359, 23-500°C at 50°C/min |
Temperatura de fusión | 205 °C Show Supplier Material materials with Temperatura de fusión of 205 °C | ISO 11357, 100°C/min |
Technological properties
| Property | ||
|---|---|---|
| Application areas | METALENTA, a unidirectionally reinforced fiberglass tape, is applied for creation an external protective and reinforcing fiberglass coating of steel pipelines with a diameter 219 to 1420 mm with an external polymer anticorrosive coating. Fiberglass coating is designated to protect the anticorrosive polymer coating from mechanical stress during the construction, operation, repair and reconstruction of the pipeline. The material is also applied for creation an external protective layer of extrusion pipes and cables to prevent surface damage during installation and operation and for creation a reinforcing layer to strengthen the structure in the production of composite pipes, sheets, panels, honeycomb structures, etc. | |
| Fillers | Glass Fiber | |