Property | Value | Comment |
---|---|---|
Densidad | 5.75 g/cm³ Show Supplier Material materials with Densidad of 5.75 g/cm³ | typical properties |
Loss on Ignition | 0.3 % Show Supplier Material materials with Loss on Ignition of 0.3 % | |
Water content | 0.2 % Show Supplier Material materials with Water content of 0.2 % |
Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 1275.0 [-] Show Supplier Material materials with Dureza Vickers of 1275.0 [-] | typical properties |
Plane-Strain Fracture Toughnes | 6.8 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 6.8 MPa·√m | typical properties |
Rheological Properties
Property | Value | Comment |
---|---|---|
Contracción | 19.0 % Show Supplier Material materials with Contracción of 19.0 % | sintering, typical properties |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminio | 0.02 Show Supplier Material materials with Aluminio of 0.02 | max. Al₂O₃ |
Calcio | 0.02 % Show Supplier Material materials with Calcio of 0.02 % | CaO |
Circonio | 96 % Show Supplier Material materials with Circonio of 96 % | ZrO₂+HfO₂ |
Hierro | 0.02 Show Supplier Material materials with Hierro of 0.02 | max. Fe₂O₃ |
Magnesio | 3.2 % Show Supplier Material materials with Magnesio of 3.2 % | MgO |
Silicona | 0.2 Show Supplier Material materials with Silicona of 0.2 | max. SiO₂ |
Titanio | 0.1 Show Supplier Material materials with Titanio of 0.1 | max. TiO₂ |
Technological properties
Property | ||
---|---|---|
Application areas | GNPGraystar’s Mg-PSZ is best used for textile ceramic pieces, high temperature steam valves, wire drawing dies, pulley cones, thermocouple protection tubes, oxygen probe protection tubes, etc. | |
Color | Yellow | |
Processing history | Sintering temperature: 1700°C |