Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.03 g/cm³ Show Material materials with Densidad of 1.03 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Dureza Shore D | 23.0 °C | 54 [-] Show Material materials with Dureza Shore D of 54 [-] | ISO 868 | ||
Elongación | 23.0 °C | 100.8 % Show Material materials with Elongación of 100.8 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 4.7 % Show Material materials with Elongation at yield of 4.7 % | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 510 J/m Show Material materials with Impact strength, Izod notched, ASTM of 510 J/m | ASTM D 256 | ||
Límite elástico | 23.0 °C | 17 MPa Show Material materials with Límite elástico of 17 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 1.78 GPa Show Material materials with Módulo de flexión of 1.78 GPa | ISO 178 | 2 mm/min, 64mm | ||
Módulo elástico | 23.0 °C | 1.89 GPa Show Material materials with Módulo elástico of 1.89 GPa | ASTM D 638 | 50 mm/min | ||
Resistencia a la tracción | 23.0 °C | 12 MPa Show Material materials with Resistencia a la tracción of 12 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA | ||
23.0 °C | 55 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 55 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 6 kJ/m² | ISO 180/1A | ||
23.0 °C | 47 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 47 kJ/m² | ISO 180/1A | |||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 3.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 3.2E-5 1/K | ISO 11359-2 | -30°C to 100°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.72E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.72E-4 1/K | ISO 11359-2 | -30°C to 100°C |
Heat deflection temperature, 1.80 MPa | 53 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 53 °C | ASTM D 648 | 1.82 MPa, 3.2 mm | |
Temperatura de reblandecimiento Vicat | 122 °C Show Material materials with Temperatura de reblandecimiento Vicat of 122 °C | ISO 306 | 10N, 50°C/hr |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.6 % Show Material materials with Contracción of 0.6 % | SABIC method | 30 min, 120°C |
Contracción transversal | 23.0 °C | 0.9 % Show Material materials with Contracción transversal of 0.9 % | SABIC method | 30 min, 120°C |
Velocidad de flujo de la masa derretida | 21 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 21 g/10min | ISO 1133 | 230°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Exterior,Recreational Vehicle | |
| Fillers | Mineral Powder | |
| Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa | |