General
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.49 [-] Show Material materials with Coeficiente de Poisson of 0.49 [-] | |||
Dureza Shore D | 23.0 °C | 56 [-] Show Material materials with Dureza Shore D of 56 [-] | max., ISO 7619-1 | ||
Elongación | 23.0 °C | 600 % Show Material materials with Elongación of 600 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 40 % Show Material materials with Elongation at yield of 40 % | ISO 527-1/-2 | ||
Límite elástico | 23.0 °C | 14 MPa Show Material materials with Límite elástico of 14 MPa | ISO 527-1/-2 | ||
Módulo elástico | 23.0 °C | 0.17 GPa Show Material materials with Módulo elástico of 0.17 GPa | ISO 527-1/-2 | ||
Resistencia a la tracción | 23.0 °C | 40 MPa Show Material materials with Resistencia a la tracción of 40 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 145 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 145 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 70 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 70 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 45 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 45 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 201 °C Show Material materials with Temperatura de fusión of 201 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 180 °C Show Material materials with Temperatura de reblandecimiento Vicat of 180 °C | ISO 306 | 90°F, 2 lbf | |||
Temperatura de transición del vidrio | -20 °C Show Material materials with Temperatura de transición del vidrio of -20 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Oxygen index: 20 %, FMVSS Class: SE - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 4.4 [-] Show Material materials with Constante dieléctrica, 1 MHz of 4.4 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 4.8 [-] Show Material materials with Constante dieléctrica, 100 Hz of 4.8 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 9E-3 [-] Show Material materials with Dissipation factor, 100Hz of 9E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.04 [-] Show Material materials with Dissipation factor, 1MHz of 0.04 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 19 kV/mm Show Material materials with Rigidez dieléctrica of 19 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 4.00E+13 Ω·cm Show Material materials with Volume resistivity of 4.00E+13 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.4 % Show Material materials with Contracción of 1.4 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.4 % Show Material materials with Contracción transversal of 1.4 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 8 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 8 g/10min | ISO 1133 | 220°C/2.16kg | |
Velocidad de flujo del volumen derretido | 7 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 7 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 230°C, Min. melt temperature: 220°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C |