General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.7 % Show Material materials with Absorción de agua of 0.7 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.19 g/cm³ Show Material materials with Densidad of 1.19 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.48 [-] Show Material materials with Coeficiente de Poisson of 0.48 [-] | |||
Dureza Shore D | 23.0 °C | 55 [-] Show Material materials with Dureza Shore D of 55 [-] | max., ISO 7619-1 | ||
Elongación | 23.0 °C | 640 % Show Material materials with Elongación of 640 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 36 % Show Material materials with Elongation at yield of 36 % | ISO 527-1/-2 | ||
Límite elástico | 23.0 °C | 15 MPa Show Material materials with Límite elástico of 15 MPa | ISO 527-1/-2 | ||
Módulo de cizallamiento | 23.0 °C | 0.07 GPa Show Material materials with Módulo de cizallamiento of 0.07 GPa | ISO 6721 | ||
Módulo de flexión | 23.0 °C | 0.2 GPa Show Material materials with Módulo de flexión of 0.2 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 0.19 GPa Show Material materials with Módulo elástico of 0.19 GPa | ISO 527-1/-2 | ||
Resistencia a desgarros | 23.0 °C | 134 kN/m Show Material materials with Resistencia a desgarros of 134 kN/m | ISO 34-1 | ||
Resistencia a desgarros transversal | 23.0 °C | 124 kN/m Show Material materials with Resistencia a desgarros transversal of 124 kN/m | ISO 34-1 | ||
Resistencia a la tracción | 23.0 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 14 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | ISO 179/1eA | ||
-6.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 30 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 110 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 110 kJ/m² | ISO 180/1A | ||
Set de compresión | 70.0 °C | 60 [-] Show Material materials with Set de compresión of 60 [-] | ISO 815 | ||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23°C, ISO 179/1eU |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -80 °C Show Material materials with Brittleness temperature of -80 °C | ISO 974 | |||
Coeficiente de dilatación térmica | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.8E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/-2 | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 78 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 78 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 51 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 51 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 90 °C Show Material materials with Relative temperature index, electrical of 90 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |||
Temperatura de fusión | 201 °C Show Material materials with Temperatura de fusión of 201 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 177 °C Show Material materials with Temperatura de reblandecimiento Vicat of 177 °C | ISO 306 | 90°F, 2 lbf | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 20 %, FMVSS Class: SE - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.3 % Show Material materials with Contracción of 1.3 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.4 % Show Material materials with Contracción transversal of 1.4 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 8.5 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 8.5 g/10min | ISO 1133 | 220°C/2.16kg | |
Velocidad de flujo del volumen derretido | 8.5 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 8.5 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 230°C, Min. melt temperature: 220°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C |