General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.72 g/cm³ Show Material materials with Densidad of 1.72 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | |
Elongación | 23.0 °C | 2.2 % Show Material materials with Elongación of 2.2 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 19.1 GPa Show Material materials with Módulo de flexión of 19.1 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 21 GPa Show Material materials with Módulo elástico of 21 GPa | ISO 527-1/-2 |
Resistencia a la flexión | 23.0 °C | 405 MPa Show Material materials with Resistencia a la flexión of 405 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 265 MPa Show Material materials with Resistencia a la tracción of 265 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 17 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 17 kJ/m² | ISO 179/1eA |
23.0 °C | 16 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 16 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 90 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 255 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 255 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 245 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 245 °C | ISO 75-1/-2 | |
Temperatura de fusión | 260 °C Show Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | first heat | |
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 60% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Min. mold temperature: 90°C, Max. mold temperature: 110°C |