General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Densidad | 20.0 °C | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | T5 | DIN 1725-2, EN 1676, EN 1706 |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Dureza Brinell | 20.0 °C | 90.0 [-] Show Material materials with Dureza Brinell of 90.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 90.0 - 110.0 [-] Show Material materials with Dureza Brinell of 90.0 - 110.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Elongación | -196.0 °C | 1.4 % Show Material materials with Elongación of 1.4 % | T5 | DIN 1725-2, EN 1676, EN 1706 | |
-196.0 °C | 1.6 % Show Material materials with Elongación of 1.6 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 1.2 % Show Material materials with Elongación of 1.2 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 1.6 % Show Material materials with Elongación of 1.6 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 1.4 % Show Material materials with Elongación of 1.4 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 0.5 % Show Material materials with Elongación of 0.5 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 0.7 % Show Material materials with Elongación of 0.7 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 1.0 - 3.0 % Show Material materials with Elongación of 1.0 - 3.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 2.2 % Show Material materials with Elongación of 2.2 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Módulo de cizallamiento | 2.8 GPa Show Material materials with Módulo de cizallamiento of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Módulo elástico | 20.0 °C | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Resistencia a la tracción | -196.0 °C | 278.0 MPa Show Material materials with Resistencia a la tracción of 278.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
-196.0 °C | 312.0 MPa Show Material materials with Resistencia a la tracción of 312.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 266.0 MPa Show Material materials with Resistencia a la tracción of 266.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 287.0 MPa Show Material materials with Resistencia a la tracción of 287.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 258.0 MPa Show Material materials with Resistencia a la tracción of 258.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 276.0 MPa Show Material materials with Resistencia a la tracción of 276.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 190.0 MPa Show Material materials with Resistencia a la tracción of 190.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 242.0 MPa Show Material materials with Resistencia a la tracción of 242.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 249.0 MPa Show Material materials with Resistencia a la tracción of 249.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 260.0 - 320.0 MPa Show Material materials with Resistencia a la tracción of 260.0 - 320.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Resistencia al cizallamiento | 20.0 °C | 181.0 MPa Show Material materials with Resistencia al cizallamiento of 181.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Calor específico | 20.0 °C | 920.0 J/(kg·K) Show Material materials with Calor específico of 920.0 J/(kg·K) | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Coeficiente de dilatación térmica | 200.0 °C | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Conductividad térmica | 20.0 °C | 150.0 - 190.0 W/(m·K) Show Material materials with Conductividad térmica of 150.0 - 190.0 W/(m·K) | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Temperatura de fusión | 505.0 - 770.0 °C Show Material materials with Temperatura de fusión of 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium |
Eléctrico
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Conductividad eléctrica | 20.0 °C | 21000000.0 - 29000000.0 S/m Show Material materials with Conductividad eléctrica of 21000000.0 - 29000000.0 S/m | T5 | DIN 1725-2, EN 1676, EN 1706 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 91.8 % Show Material materials with Aluminio of 91.8 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Cobre | 0.05 Show Material materials with Cobre of 0.05 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Hierro | 0.5 Show Material materials with Hierro of 0.5 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Magnesio | 0.4 - 0.8 % Show Material materials with Magnesio of 0.4 - 0.8 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Manganeso | 0.001 - 0.4 % Show Material materials with Manganeso of 0.001 - 0.4 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Silicona | 5.0 - 6.0 % Show Material materials with Silicona of 5.0 - 6.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Titanio | 0.001 - 0.2 % Show Material materials with Titanio of 0.001 - 0.2 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Zinc | 0.1 Show Material materials with Zinc of 0.1 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Technological properties
Property | ||
---|---|---|
Processing methods | permanent mould casting |