DIN 1725-1 Grade 3.3207 T5

Want to keep this datasheet? Save it now in your required format

Description

E-AlMgSi0,5 is ensured by the German electrotechnical commission as alloy for electro-technology according to DIN 40 501 part of 1 to part of 4. This cold and hothardenable material reaches mechanical strength in range of 200 to 250 MPa with A5-elongation at break of approx. 10 %. In hot and/or cold hardend state is this alloy only limited formable, in the soft material condition however well. Weldability, corrosion resistance and anodising ability of this material are good. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperatures warm ageing: 4 to 16 h at 155 to 190 °C. Application: The alloy E-AlMgSi0,5 is used with priority for bus bars. Because of the good extruding bar of this material as flat -, profile or tubing bus bars. Electro-technology (bus bars)

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad	20.0 °C	2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Dureza Brinell	20.0 °C	45.0 - 65.0 [-] Show Material materials with Dureza Brinell of 45.0 - 65.0 [-]	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod
	20.0 °C	65.0 - 90.0 [-] Show Material materials with Dureza Brinell of 65.0 - 90.0 [-]	T5	DIN 1725-1, EN 573-3, EN 573-4	Rod
	20.0 °C	65.0 - 80.0 [-] Show Material materials with Dureza Brinell of 65.0 - 80.0 [-]	T5	DIN 1725-1, EN 573-3, EN 573-4	Tube
Elongación	20.0 °C	8.0 % Show Material materials with Elongación of 8.0 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Tube
	20.0 °C	10.0 % Show Material materials with Elongación of 10.0 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube	A10
	20.0 °C	12.0 % Show Material materials with Elongación of 12.0 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Módulo de cizallamiento	20.0 °C	25.5 GPa Show Material materials with Módulo de cizallamiento of 25.5 GPa	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa				Typical for Wrought 6000 Series Aluminium
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Resistencia a la tracción	20.0 °C	170.0 - 220.0 MPa Show Material materials with Resistencia a la tracción of 170.0 - 220.0 MPa	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod
	20.0 °C	215.0 - 280.0 MPa Show Material materials with Resistencia a la tracción of 215.0 - 280.0 MPa	T5	DIN 1725-1, EN 573-3, EN 573-4	Rod, Tube

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico	20.0 °C	898.0 J/(kg·K) Show Material materials with Calor específico of 898.0 J/(kg·K)	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Coeficiente de dilatación térmica		1.6e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.4e-05 1/K				Typical for Wrought 6000 Series Aluminium
Conductividad térmica	20.0 °C	220.0 W/(m·K) Show Material materials with Conductividad térmica of 220.0 W/(m·K)	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Temperatura de fusión		555.0 - 655.0 °C Show Material materials with Temperatura de fusión of 555.0 - 655.0 °C				Typical for Wrought 6000 Series Aluminium

Eléctrico

Property	Value	Comment
Conductividad eléctrica	21000000.0 - 34000000.0 S/m Show Material materials with Conductividad eléctrica of 21000000.0 - 34000000.0 S/m	Typical for Wrought 6000 Series Aluminium
Resistividad eléctrica	2.9e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.9e-08 - 5e-08 Ω·m	Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.05 Show Material materials with Cobre of 0.05	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Hierro	0.1 - 0.3 % Show Material materials with Hierro of 0.1 - 0.3 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Magnesio	0.35 - 0.6 % Show Material materials with Magnesio of 0.35 - 0.6 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Manganeso	0.05 Show Material materials with Manganeso of 0.05	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Silicona	0.3 - 0.6 % Show Material materials with Silicona of 0.3 - 0.6 %	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Zinc	0.1 Show Material materials with Zinc of 0.1	T5	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube

Technological properties

Property

Workability

Excellent workability.