DIN 1725-1 Grade 3.2316 T6

Want to keep this datasheet? Save it now in your required format

Description

This cold and hot hardenable material reaches mechanical strength of 200 to 250 MPa with A5-elongation at break of approx. 10 %. In warm and/or cold-hardened condition is this alloy only limited formable, in the soft material condition however well. Weldability, corrosion resistance and anodisingability of this material are good. However this alloy is used more for rivet or bolt joints, because of the destabilization danger in the welding zone. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperature hot ageing: 4 to 16 h at 155 to 190 °C Application: In the construction of vehicles for vehicle floors, stands, commercial motor vehicle superstructures of all kinds, trim. In the building industry for window, doors, window walls, shower cubicles, fences. In the building of rail-mounted vehicles for car boxes. In shipbuilding for sail masts, sail trees. In mechanical engineering (including building of forms) and for metal goods (e.g. building fittings, table-ware, flow pressed parts, reflectors).

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad	20.0 °C	2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Dureza Brinell	20.0 °C	75.0 [-] Show Material materials with Dureza Brinell of 75.0 [-]	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Elongación	20.0 °C	8.0 % Show Material materials with Elongación of 8.0 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Módulo de cizallamiento	20.0 °C	27.0 Show Material materials with Módulo de cizallamiento of 27.0	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Módulo elástico	20.0 °C	73.0 Show Material materials with Módulo elástico of 73.0	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Resistencia a la tracción	20.0 °C	275.0 MPa Show Material materials with Resistencia a la tracción of 275.0 MPa	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico		887.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 887.0 - 963.0 J/(kg·K)				Typical for Wrought 6000 Series Aluminium
Coeficiente de dilatación térmica		1.6e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.4e-05 1/K				Typical for Wrought 6000 Series Aluminium
Conductividad térmica	20.0 °C	170.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 - 220.0 W/(m·K)	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Temperatura de fusión		555.0 - 655.0 °C Show Material materials with Temperatura de fusión of 555.0 - 655.0 °C				Typical for Wrought 6000 Series Aluminium

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Conductividad eléctrica	20.0 °C	24000000.0 - 32000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 - 32000000.0 S/m	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Resistividad eléctrica		2.9e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.9e-08 - 5e-08 Ω·m				Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.05 Show Material materials with Cobre of 0.05	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Cromo	0.03 Show Material materials with Cromo of 0.03	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Hierro	0.25 Show Material materials with Hierro of 0.25	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Magnesio	0.6 - 0.7 % Show Material materials with Magnesio of 0.6 - 0.7 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Manganeso	0.15 Show Material materials with Manganeso of 0.15	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Silicona	0.8 - 1.0 % Show Material materials with Silicona of 0.8 - 1.0 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Titanio	0.05 Show Material materials with Titanio of 0.05	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Zinc	0.1 Show Material materials with Zinc of 0.1	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Technological properties

Property

Workability

Excellent workability.