General
Property | Value | Comment |
---|---|---|
Densidad | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | Typical for Wrought 6000 Series Aluminium |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Elongación | -75.0 °C | 10.0 % Show Material materials with Elongación of 10.0 % | T5 | DIN 1725-1 | Seamless Tube | Transverse |
-75.0 °C | 14.0 % Show Material materials with Elongación of 14.0 % | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube | ||
20.0 °C | 10.0 % Show Material materials with Elongación of 10.0 % | T5 | DIN 1725-1 | Seamless Tube | Transverse | |
20.0 °C | 14.0 % Show Material materials with Elongación of 14.0 % | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube | ||
50.0 °C | 10.0 % Show Material materials with Elongación of 10.0 % | T5 | DIN 1725-1 | Seamless Tube | Transverse | |
50.0 °C | 14.0 % Show Material materials with Elongación of 14.0 % | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube | ||
100.0 °C | 14.0 % Show Material materials with Elongación of 14.0 % | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube | ||
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Resistencia a la tracción | -75.0 °C | 275.0 MPa Show Material materials with Resistencia a la tracción of 275.0 MPa | T5 | DIN 1725-1 | Seamless Tube | |
-75.0 °C | 275.0 MPa Show Material materials with Resistencia a la tracción of 275.0 MPa | T5 | DIN 1725-1 | Seamless Tube | Transverse | |
-75.0 °C | 310.0 MPa Show Material materials with Resistencia a la tracción of 310.0 MPa | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube | ||
-75.0 °C | 310.0 MPa Show Material materials with Resistencia a la tracción of 310.0 MPa | T5 | DIN 1725-1 | Seamless Tube | Transverse | |
20.0 °C | 225.0 MPa Show Material materials with Resistencia a la tracción of 225.0 MPa | T5 | DIN 1725-1 | Tube | ||
20.0 °C | 250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | T5 | DIN 1725-1 | Rod, Seamless Tube | ||
20.0 °C | 275.0 MPa Show Material materials with Resistencia a la tracción of 275.0 MPa | T5 | DIN 1725-1 | Seamless Tube | ||
20.0 °C | 275.0 MPa Show Material materials with Resistencia a la tracción of 275.0 MPa | T5 | DIN 1725-1 | Seamless Tube | Transverse | |
20.0 °C | 310.0 MPa Show Material materials with Resistencia a la tracción of 310.0 MPa | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube | ||
20.0 °C | 310.0 MPa Show Material materials with Resistencia a la tracción of 310.0 MPa | T5 | DIN 1725-1 | Seamless Tube | Transverse | |
20.0 °C | 390.0 MPa Show Material materials with Resistencia a la tracción of 390.0 MPa | T5 | DIN 1725-1 | Rod | ||
50.0 °C | 190.0 MPa Show Material materials with Resistencia a la tracción of 190.0 MPa | T5 | DIN 1725-1 | Rod | ||
50.0 °C | 220.0 MPa Show Material materials with Resistencia a la tracción of 220.0 MPa | T5 | DIN 1725-1 | |||
50.0 °C | 250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | T5 | DIN 1725-1 | Rod, Seamless Tube | ||
50.0 °C | 250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | T5 | DIN 1725-1 | Seamless Tube | Transverse | |
50.0 °C | 260.0 MPa Show Material materials with Resistencia a la tracción of 260.0 MPa | T5 | DIN 1725-1 | Rod | ||
50.0 °C | 280.0 MPa Show Material materials with Resistencia a la tracción of 280.0 MPa | T5 | DIN 1725-1 | Tube, Seamless Tube | ||
50.0 °C | 280.0 MPa Show Material materials with Resistencia a la tracción of 280.0 MPa | T5 | DIN 1725-1 | Seamless Tube | Transverse | |
50.0 °C | 290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | T5 | DIN 1725-1 | Rod, Tube | ||
50.0 °C | 300.0 MPa Show Material materials with Resistencia a la tracción of 300.0 MPa | T5 | DIN 1725-1 | Rod, Tube | ||
100.0 °C | 180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa | T5 | DIN 1725-1 | Rod | ||
100.0 °C | 210.0 MPa Show Material materials with Resistencia a la tracción of 210.0 MPa | T5 | DIN 1725-1 | Rod | ||
100.0 °C | 250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | T5 | DIN 1725-1 | Rod, Seamless Tube | ||
100.0 °C | 280.0 MPa Show Material materials with Resistencia a la tracción of 280.0 MPa | T5 | DIN 1725-1 | Tube, Seamless Tube | ||
100.0 °C | 290.0 MPa Show Material materials with Resistencia a la tracción of 290.0 MPa | T5 | DIN 1725-1 | Rod, Tube | ||
100.0 °C | 335.0 MPa Show Material materials with Resistencia a la tracción of 335.0 MPa | T5 | DIN 1725-1 | Rod |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Calor específico | 887.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium |
Coeficiente de dilatación térmica | 1.6e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 6000 Series Aluminium |
Conductividad térmica | 170.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Temperatura de fusión | 555.0 - 655.0 °C Show Material materials with Temperatura de fusión of 555.0 - 655.0 °C | Typical for Wrought 6000 Series Aluminium |
Eléctrico
Property | Value | Comment |
---|---|---|
Conductividad eléctrica | 21000000.0 - 34000000.0 S/m Show Material materials with Conductividad eléctrica of 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Resistividad eléctrica | 2.9e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Cobre | 0.05 Show Material materials with Cobre of 0.05 | T5 | DIN 1725-1 | Tube |
0.1 Show Material materials with Cobre of 0.1 | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube | |
Cromo | 0.1 - 0.25 % Show Material materials with Cromo of 0.1 - 0.25 % | T5 | DIN 1725-1 | Rod, Tube |
0.1 - 0.2 % Show Material materials with Cromo of 0.1 - 0.2 % | T5 | DIN 1725-1 | Seamless Tube | |
0.2 % Show Material materials with Cromo of 0.2 % | T5 | DIN 1725-1 | Seamless Tube | |
0.25 % Show Material materials with Cromo of 0.25 % | T5 | DIN 1725-1 | Rod | |
Hierro | 0.4 Show Material materials with Hierro of 0.4 | T5 | DIN 1725-1 | Seamless Tube, Tube |
0.5 Show Material materials with Hierro of 0.5 | T5 | DIN 1725-1 | Rod, Tube | |
Magnesio | 0.6 - 1.2 % Show Material materials with Magnesio of 0.6 - 1.2 % | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube |
1.2 % Show Material materials with Magnesio of 1.2 % | T5 | DIN 1725-1 | Seamless Tube | |
Manganeso | 0.4 - 1.0 % Show Material materials with Manganeso of 0.4 - 1.0 % | T5 | DIN 1725-1 | Rod, Tube |
0.4 - 0.8 % Show Material materials with Manganeso of 0.4 - 0.8 % | T5 | DIN 1725-1 | Seamless Tube | |
0.8 % Show Material materials with Manganeso of 0.8 % | T5 | DIN 1725-1 | Seamless Tube | |
Silicona | 0.7 - 1.3 % Show Material materials with Silicona of 0.7 - 1.3 % | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube |
0.75 - 1.3 % Show Material materials with Silicona of 0.75 - 1.3 % | T5 | DIN 1725-1 | Tube | |
1.3 % Show Material materials with Silicona of 1.3 % | T5 | DIN 1725-1 | Seamless Tube | |
Titanio | 0.1 Show Material materials with Titanio of 0.1 | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube |
Zinc | 0.2 Show Material materials with Zinc of 0.2 | T5 | DIN 1725-1 | Rod, Tube, Seamless Tube |
Technological properties
Property | ||
---|---|---|
Workability | Excellent workability. |