DIN 1725-1 Grade 3.3208 T6

Want to keep this datasheet? Save it now in your required format

Description

The alloy Al99,9MgSi belongs to the standardised aluminum shining materials. Aluminum alloys being based on aluminum with a minimum purity of 99,85 %, can be polished after mechanical polishing chemically or electrolytically to high gloss. The produced gloss degree must, in order to remain preserved, be afterwards anodised. The degree of arranged reflection (grade of gloss), depends again on the degree of purity and the anodising layer thickness. It is cold and hot hardenabel. Strength grade up to F 24 can be achieved by hot ageing. The alloy Al99,9MgSi has a very good corrosion resistance and is well cold and hot formable. This alloy is standardised only as extruded section (DIN 1748 T1 and T2) and piece of drop forge (DIN 1749 T1 and T2). Application: For decoration goods (trim) and Bijouterie articles for metal goods of all kinds (e.g. building fittings, table-ware, flow pressed parts) and for reflectors.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad	20.0 °C	2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Dureza Brinell	20.0 °C	70.0 [-] Show Material materials with Dureza Brinell of 70.0 [-]	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Elongación	20.0 °C	14.0 % Show Material materials with Elongación of 14.0 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Módulo de cizallamiento		26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa				Typical for Wrought 6000 Series Aluminium
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa				Typical for Wrought 6000 Series Aluminium
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Resistencia a la tracción	20.0 °C	235.0 MPa Show Material materials with Resistencia a la tracción of 235.0 MPa	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Aplicaciones térmicas

Property	Value	Comment
Calor específico	887.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 887.0 - 963.0 J/(kg·K)	Typical for Wrought 6000 Series Aluminium
Coeficiente de dilatación térmica	1.6e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.4e-05 1/K	Typical for Wrought 6000 Series Aluminium
Conductividad térmica	170.0 - 220.0 W/(m·K) Show Material materials with Conductividad térmica of 170.0 - 220.0 W/(m·K)	Typical for Wrought 6000 Series Aluminium
Temperatura de fusión	555.0 - 655.0 °C Show Material materials with Temperatura de fusión of 555.0 - 655.0 °C	Typical for Wrought 6000 Series Aluminium

Eléctrico

Property	Value	Comment
Conductividad eléctrica	21000000.0 - 34000000.0 S/m Show Material materials with Conductividad eléctrica of 21000000.0 - 34000000.0 S/m	Typical for Wrought 6000 Series Aluminium
Resistividad eléctrica	2.9e-08 - 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 2.9e-08 - 5e-08 Ω·m	Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.05 - 0.2 % Show Material materials with Cobre of 0.05 - 0.2 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Hierro	0.04 Show Material materials with Hierro of 0.04	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Magnesio	0.35 - 0.7 % Show Material materials with Magnesio of 0.35 - 0.7 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Manganeso	0.03 Show Material materials with Manganeso of 0.03	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Silicona	0.35 - 0.7 % Show Material materials with Silicona of 0.35 - 0.7 %	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Titanio	0.01 Show Material materials with Titanio of 0.01	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging
Zinc	0.04 Show Material materials with Zinc of 0.04	T6	DIN 1725-1, EN 573-3, EN 573-4	Forging

Technological properties

Property

Workability

Excellent workability.