DIN 1725-1 Grade 3.3525 F

Want to keep this datasheet? Save it now in your required format

Description

The alloy AlMg2Mn0,3 has similar characteristics as the alloy AlMg1,8. The additive of Mn causes an increase of the heat resistance of the material apart from a strength increase with the products of extruding. The material is characterised by a good corrosion resistance. It is sea water steady and steady against saline atmosphere. With the Mg content the strength increases, the cold forming capacity decreases. The alloy is nature hard, i.e. that only by a cold forming shaping however by a purposeful heat treatment a strength increase cannot be attained. The splinter-giving workability and the weldability are improved with increasing Mg content. Application: For metal goods (including table-ware), in food industry (including commercial devices). For transport containers e.g. rolling barrels, in the packaging industry as cans as well as for describe (e.g. road signs).

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM,AluKey.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Lectura sugerida

6061-T6 Aluminium – The Ultimate Guide

7075-T6 Aluminium: Overview & Properties

Aircraft Aluminium Grades

Cast vs. Wrought Aluminium: Standards, Properties and Applications

Precipitation Hardening (Age Hardening)

Mostrar todo

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad		2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coeficiente de Poisson		0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-]				Typical for Wrought 5000 Series Aluminium
Dureza Brinell		45.0 [-] Show Material materials with Dureza Brinell of 45.0 [-]	F	EN 573-3, EN 570
	20.0 °C	40.0 [-] Show Material materials with Dureza Brinell of 40.0 [-]	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Elongación		14.0 % Show Material materials with Elongación of 14.0 %	F	EN 573-3, EN 755		A50
		16.0 % Show Material materials with Elongación of 16.0 %	F	EN 573-3, EN 755		A100
	20.0 °C	12.0 % Show Material materials with Elongación of 12.0 %	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube	A10
	20.0 °C	14.0 % Show Material materials with Elongación of 14.0 %	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Módulo de cizallamiento		26.3 GPa Show Material materials with Módulo de cizallamiento of 26.3 GPa	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	26.5 GPa Show Material materials with Módulo de cizallamiento of 26.5 GPa	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Módulo elástico		70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Resistencia a la tracción		160.0 MPa Show Material materials with Resistencia a la tracción of 160.0 MPa	F	EN 573-3, EN 485, EN 755
		170.0 - 230.0 MPa Show Material materials with Resistencia a la tracción of 170.0 - 230.0 MPa	F	EN 573-3, EN 1715-3
	20.0 °C	150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico	20.0 °C	921.0 J/(kg·K) Show Material materials with Calor específico of 921.0 J/(kg·K)	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Coeficiente de dilatación térmica	20 °C	2.3699999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3699999999999997e-05 1/K	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
	100 °C	2.3699999999999997e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3699999999999997e-05 1/K	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
Conductividad térmica		140.0 - 160.0 W/(m·K) Show Material materials with Conductividad térmica of 140.0 - 160.0 W/(m·K)	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	167.0 W/(m·K) Show Material materials with Conductividad térmica of 167.0 W/(m·K)	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Temperatura de fusión		610.0 - 650.0 °C Show Material materials with Temperatura de fusión of 610.0 - 650.0 °C	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
Temperatura máx. de funcionamiento		150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C				Typical for Wrought 5000 Series Aluminium

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Conductividad eléctrica		25000000.0 - 30000000.0 S/m Show Material materials with Conductividad eléctrica of 25000000.0 - 30000000.0 S/m	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
	20.0 °C	26000000.0 S/m Show Material materials with Conductividad eléctrica of 26000000.0 S/m	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
Resistividad eléctrica		3.33e-08 - 4e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.33e-08 - 4e-08 Ω·m	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755

Chemical properties

Property	Value	Condition	Related Standards	Shape
Cobre	0.15 % Show Material materials with Cobre of 0.15 %	F	DIN 1725-1, EN 573-3, EN 573-4, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Cromo	0.15 % Show Material materials with Cromo of 0.15 %	F	DIN 1725-1, EN 573-3, EN 573-4, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Hierro	0.5 % Show Material materials with Hierro of 0.5 %	F	DIN 1725-1, EN 573-3, EN 573-4	Profile, Rod, Tube
	0.50 % Show Material materials with Hierro of 0.50 %	F	EN 573-3, EN 1715-3, EN 485, EN 570, EN 755
Magnesio	1.7 - 2.4 % Show Material materials with Magnesio of 1.7 - 2.4 %	F	DIN 1725-1, EN 573-3, EN 573-4, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Manganeso	0.1 - 0.5 % Show Material materials with Manganeso of 0.1 - 0.5 %	F	DIN 1725-1, EN 573-3, EN 573-4, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Silicona	0.4 % Show Material materials with Silicona of 0.4 %	F	DIN 1725-1, EN 573-3, EN 573-4, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Titanio	0.15 % Show Material materials with Titanio of 0.15 %	F	DIN 1725-1, EN 573-3, EN 573-4, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube
Zinc	0.15 % Show Material materials with Zinc of 0.15 %	F	DIN 1725-1, EN 573-3, EN 573-4, EN 1715-3, EN 485, EN 570, EN 755	Profile, Rod, Tube

Technological properties

Property
Anodizing	decorative: sufficient, Protective: very good
Brazing	hard brazing (with flux/ without flux): sufficient / poor, friction soldering: good, soft brazing with flux: sufficient
Corrosion properties	Seawater: good, weathering: very good
Workability	Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / acceptable (H12)

Looking for suppliers of this material? Click to see 2 supplier of DIN 1725-1 Grade 3.3525 F on Matmatch