General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 20.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Densidad of 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 20.0 °C | 0.29 [-] Show Material materials with Coeficiente de Poisson of 0.29 [-] | Typical for Low Carbon Steel |
Dureza Vickers | 20.0 °C | 100 [-] Show Material materials with Dureza Vickers of 100 [-] | |
Elongación | 20.0 °C | 37 % Show Material materials with Elongación of 37 % | |
Elongación A50 | 20.0 °C | 36 % Show Material materials with Elongación A50 of 36 % | |
Elongación A80 | 20.0 °C | 34 % Show Material materials with Elongación A80 of 34 % | |
Límite elástico | 20.0 °C | 140 MPa Show Material materials with Límite elástico of 140 MPa | |
Módulo elástico | 20.0 °C | 200 - 215 GPa Show Material materials with Módulo elástico of 200 - 215 GPa | Typical for Low Carbon Steel |
Resistencia a la tracción | 20.0 °C | 270 - 370 MPa Show Material materials with Resistencia a la tracción of 270 - 370 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 20.0 °C | 1.32E-5 - 1.38E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Temperatura de fusión | 1480 - 1526 °C Show Material materials with Temperatura de fusión of 1480 - 1526 °C | Typical for Low Carbon Steel |
Magnético
Property | Value | Comment |
---|---|---|
Temperatura de Curie | 770 °C Show Material materials with Temperatura de Curie of 770 °C | Typical for Low Carbon Steel |