General
Property | Temperature | Value |
---|---|---|
Densidad | 20.0 °C | 7.1 g/cm³ Show Material materials with Densidad of 7.1 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 20.0 °C | 0.28 [-] Show Material materials with Coeficiente de Poisson of 0.28 [-] | |
Compressive yield strength | 20.0 °C | 700 MPa Show Material materials with Compressive yield strength of 700 MPa | |
Elongación | 20.0 °C | 18 % Show Material materials with Elongación of 18 % | |
Límite elástico Rp 0,2 | 20.0 °C | 250 MPa Show Material materials with Límite elástico Rp 0,2 of 250 MPa | |
Módulo de cizallamiento | 23.0 °C | 63 - 66 GPa Show Material materials with Módulo de cizallamiento of 63 - 66 GPa | Typical for Ductile (Nodular) Cast Iron |
Módulo elástico | 20.0 °C | 169 GPa Show Material materials with Módulo elástico of 169 GPa | |
Resistencia a la tracción | 20.0 °C | 400 MPa Show Material materials with Resistencia a la tracción of 400 MPa | |
Resistencia al cizallamiento | 20.0 °C | 360 MPa Show Material materials with Resistencia al cizallamiento of 360 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 500.0 °C | 515 J/(kg·K) Show Material materials with Calor específico of 515 J/(kg·K) | |
Coeficiente de dilatación térmica | 400.0 °C | 1.25E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.25E-5 1/K | |
Conductividad térmica | 300.0 °C | 36.2 W/(m·K) Show Material materials with Conductividad térmica of 36.2 W/(m·K) | |
Temperatura de fusión | 1150 - 1200 °C Show Material materials with Temperatura de fusión of 1150 - 1200 °C | Typical for Ductile (Nodular) Cast Iron |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 20.0 °C | 5E-7 Ω·m Show Material materials with Resistividad eléctrica of 5E-7 Ω·m |