General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Densidad | 20.0 °C | 2.65 g/cm³ Show Material materials with Densidad of 2.65 g/cm³ | T5 | DIN 1725-2, EN 1676, EN 1706 |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Dureza Brinell | 20.0 °C | 70.0 [-] Show Material materials with Dureza Brinell of 70.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 75.0 [-] Show Material materials with Dureza Brinell of 75.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 75.0 - 110.0 [-] Show Material materials with Dureza Brinell of 75.0 - 110.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 80.0 - 110.0 [-] Show Material materials with Dureza Brinell of 80.0 - 110.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 80.0 [-] Show Material materials with Dureza Brinell of 80.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 80.0 - 115.0 [-] Show Material materials with Dureza Brinell of 80.0 - 115.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Elongación | 20.0 °C | 2.0 % Show Material materials with Elongación of 2.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 2.0 - 5.0 % Show Material materials with Elongación of 2.0 - 5.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 3.0 % Show Material materials with Elongación of 3.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 3.0 - 6.0 % Show Material materials with Elongación of 3.0 - 6.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 5.0 - 9.0 % Show Material materials with Elongación of 5.0 - 9.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Módulo de cizallamiento | 2.8 GPa Show Material materials with Módulo de cizallamiento of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Módulo elástico | 20.0 °C | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Resistencia a la tracción | 20.0 °C | 230.0 MPa Show Material materials with Resistencia a la tracción of 230.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 230.0 - 310.0 MPa Show Material materials with Resistencia a la tracción of 230.0 - 310.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 250.0 - 340.0 MPa Show Material materials with Resistencia a la tracción of 250.0 - 340.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 260.0 - 320.0 MPa Show Material materials with Resistencia a la tracción of 260.0 - 320.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Resistencia al cizallamiento | 20.0 °C | 220.0 MPa Show Material materials with Resistencia al cizallamiento of 220.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Calor específico | 20.0 °C | 920.0 J/(kg·K) Show Material materials with Calor específico of 920.0 J/(kg·K) | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Coeficiente de dilatación térmica | 200.0 °C | 2.2e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2e-05 1/K | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Conductividad térmica | 20.0 °C | 160.0 - 170.0 W/(m·K) Show Material materials with Conductividad térmica of 160.0 - 170.0 W/(m·K) | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Temperatura de fusión | 505.0 - 770.0 °C Show Material materials with Temperatura de fusión of 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium |
Eléctrico
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Conductividad eléctrica | 20.0 °C | 22000000.0 - 24000000.0 S/m Show Material materials with Conductividad eléctrica of 22000000.0 - 24000000.0 S/m | T5 | DIN 1725-2, EN 1676, EN 1706 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 91.4 % Show Material materials with Aluminio of 91.4 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Cobre | 0.05 Show Material materials with Cobre of 0.05 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Hierro | 0.18 Show Material materials with Hierro of 0.18 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Magnesio | 0.25 - 0.45 % Show Material materials with Magnesio of 0.25 - 0.45 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Manganeso | 0.1 Show Material materials with Manganeso of 0.1 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Silicona | 6.5 - 7.5 % Show Material materials with Silicona of 6.5 - 7.5 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Titanio | 0.001 - 0.2 % Show Material materials with Titanio of 0.001 - 0.2 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Zinc | 0.07 Show Material materials with Zinc of 0.07 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Technological properties
Property | ||
---|---|---|
Processing methods | investment casting, sample taken from casting |