Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 - 90.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 - 90.0 MPa | F | EN 1706 | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Cast 5xx.x Series Aluminium | |||
Dureza Brinell | 60.0 [-] Show Material materials with Dureza Brinell of 60.0 [-] | F | EN 1706 | ||
65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-] | F | EN 1706 | |||
20.0 °C | 55.0 [-] Show Material materials with Dureza Brinell of 55.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 60.0 [-] Show Material materials with Dureza Brinell of 60.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 60.0 - 75.0 [-] Show Material materials with Dureza Brinell of 60.0 - 75.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 65.0 - 85.0 [-] Show Material materials with Dureza Brinell of 65.0 - 85.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
Elongación | -196.0 °C | 2.9 % Show Material materials with Elongación of 2.9 % | F | DIN 1725-2, EN 1676, EN 1706 | |
-196.0 °C | 3.3 % Show Material materials with Elongación of 3.3 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 2.6 % Show Material materials with Elongación of 2.6 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 3.9 % Show Material materials with Elongación of 3.9 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 3.4 % Show Material materials with Elongación of 3.4 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 4.3 % Show Material materials with Elongación of 4.3 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
3.0 % Show Material materials with Elongación of 3.0 % | F | EN 1706 | A50 | ||
20.0 °C | 1.0 % Show Material materials with Elongación of 1.0 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 2.0 - 5.0 % Show Material materials with Elongación of 2.0 - 5.0 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 2.0 - 4.0 % Show Material materials with Elongación of 2.0 - 4.0 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 3.0 % Show Material materials with Elongación of 3.0 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 3.8 % Show Material materials with Elongación of 3.8 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | F | EN 1706 | ||
20.0 °C | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
Resistencia a la tracción | -196.0 °C | 198.0 MPa Show Material materials with Resistencia a la tracción of 198.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | |
-196.0 °C | 219.0 MPa Show Material materials with Resistencia a la tracción of 219.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 175.0 MPa Show Material materials with Resistencia a la tracción of 175.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
-120.0 °C | 203.0 MPa Show Material materials with Resistencia a la tracción of 203.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 172.0 MPa Show Material materials with Resistencia a la tracción of 172.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
-50.0 °C | 187.0 MPa Show Material materials with Resistencia a la tracción of 187.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
160.0 MPa Show Material materials with Resistencia a la tracción of 160.0 MPa | F | EN 1706 | |||
180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa | F | EN 1706 | |||
20.0 °C | 140.0 MPa Show Material materials with Resistencia a la tracción of 140.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 157.0 MPa Show Material materials with Resistencia a la tracción of 157.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 160.0 - 200.0 MPa Show Material materials with Resistencia a la tracción of 160.0 - 200.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 180.0 - 240.0 MPa Show Material materials with Resistencia a la tracción of 180.0 - 240.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 184.0 MPa Show Material materials with Resistencia a la tracción of 184.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
Resistencia al cizallamiento | 20.0 °C | 138.0 MPa Show Material materials with Resistencia al cizallamiento of 138.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 150.0 MPa Show Material materials with Resistencia al cizallamiento of 150.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Calor específico | 930.0 J/(kg·K) Show Material materials with Calor específico of 930.0 J/(kg·K) | F | EN 1706 | |
20.0 °C | 930.0 J/(kg·K) Show Material materials with Calor específico of 930.0 J/(kg·K) | F | DIN 1725-2, EN 1676, EN 1706 | |
Coeficiente de dilatación térmica | 20 °C | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 |
100 °C | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
200.0 °C | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
Conductividad térmica | 110.0 - 140.0 W/(m·K) Show Material materials with Conductividad térmica of 110.0 - 140.0 W/(m·K) | F | EN 1706 | |
20.0 °C | 110.0 - 130.0 W/(m·K) Show Material materials with Conductividad térmica of 110.0 - 130.0 W/(m·K) | F | DIN 1725-2, EN 1676, EN 1706 | |
Temperatura de fusión | 550.0 - 630.0 °C Show Material materials with Temperatura de fusión of 550.0 - 630.0 °C | F | EN 1706 |
Eléctrico
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Conductividad eléctrica | 15000000.0 - 21000000.0 S/m Show Material materials with Conductividad eléctrica of 15000000.0 - 21000000.0 S/m | F | EN 1706 | |
20.0 °C | 15000000.0 - 19000000.0 S/m Show Material materials with Conductividad eléctrica of 15000000.0 - 19000000.0 S/m | F | DIN 1725-2, EN 1676, EN 1706 | |
Resistividad eléctrica | 4.76e-08 - 6.67e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.76e-08 - 6.67e-08 Ω·m | F | EN 1706 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 91.6 % Show Material materials with Aluminio of 91.6 % | F | DIN 1725-2, EN 1676, EN 1706 |
Cobre | 0.05 % Show Material materials with Cobre of 0.05 % | F | DIN 1725-2, EN 1676, EN 1706 |
Hierro | 0.5 % Show Material materials with Hierro of 0.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
0.50 % Show Material materials with Hierro of 0.50 % | F | EN 1706 | |
Magnesio | 4.5 - 5.5 % Show Material materials with Magnesio of 4.5 - 5.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Manganeso | 0.001 - 0.4 % Show Material materials with Manganeso of 0.001 - 0.4 % | F | DIN 1725-2, EN 1676, EN 1706 |
Silicona | 0.9 - 1.5 % Show Material materials with Silicona of 0.9 - 1.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Titanio | 0.001 - 0.2 % Show Material materials with Titanio of 0.001 - 0.2 % | F | DIN 1725-2, EN 1676, EN 1706 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | F | DIN 1725-2, EN 1676, EN 1706 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: good | |
Corrosion properties | general: excellent | |
General machinability | after thermal treatment: excellent | |
Processing methods | permanent mould casting |