EN 1652 Grade CuZn39Pb0.5 R400

Want to keep this datasheet? Save it now in your required format

Description

Material CuZn39Pb0,5, mat. No. CW610N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb0,5, mat. No. 2.0372 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: moderately machinability: good hard soldering: moderately soft soldering: very good TIG-welding: moderately burnishing: very good Application: For plug pins, fitting parts, rivets, condenser plates, floor plate screeding and drawing instruments.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value
Densidad	20.0 °C	8.4 g/cm³ Show Material materials with Densidad of 8.4 g/cm³

Mecánica

Property	Temperature	Value
Dureza Vickers	20.0 °C	110 [-] Show Material materials with Dureza Vickers of 110 [-]
Elongación	20.0 °C	20 - 23 % Show Material materials with Elongación of 20 - 23 %
Elongación A50	20.0 °C	14 % Show Material materials with Elongación A50 of 14 %
Elongación transversal	20.0 °C	23 % Show Material materials with Elongación transversal of 23 %
Límite elástico Rp 0,2	20.0 °C	200 MPa Show Material materials with Límite elástico Rp 0,2 of 200 MPa
	50.0 °C	200 MPa Show Material materials with Límite elástico Rp 0,2 of 200 MPa
	100.0 °C	190 MPa Show Material materials with Límite elástico Rp 0,2 of 190 MPa
	150.0 °C	180 MPa Show Material materials with Límite elástico Rp 0,2 of 180 MPa

Límite elástico transversal Rp 0,2	20.0 °C	200 - 240 MPa Show Material materials with Límite elástico transversal Rp 0,2 of 200 - 240 MPa
	50.0 °C	200 MPa Show Material materials with Límite elástico transversal Rp 0,2 of 200 MPa
	100.0 °C	190 MPa Show Material materials with Límite elástico transversal Rp 0,2 of 190 MPa
	150.0 °C	180 MPa Show Material materials with Límite elástico transversal Rp 0,2 of 180 MPa
	Unlock all property charts
Módulo de cizallamiento	20.0 °C	37 GPa Show Material materials with Módulo de cizallamiento of 37 GPa
Módulo elástico	-195.0 °C	108 GPa Show Material materials with Módulo elástico of 108 GPa
	-100.0 °C	106 GPa Show Material materials with Módulo elástico of 106 GPa
	20.0 °C	102 - 105 GPa Show Material materials with Módulo elástico of 102 - 105 GPa
	50.0 °C	100 GPa Show Material materials with Módulo elástico of 100 GPa
	100.0 °C	93 GPa Show Material materials with Módulo elástico of 93 GPa
	150.0 °C	91 GPa Show Material materials with Módulo elástico of 91 GPa
	200.0 °C	89 GPa Show Material materials with Módulo elástico of 89 GPa
	250.0 °C	83 GPa Show Material materials with Módulo elástico of 83 GPa
	Unlock all property charts
Resistencia a la tracción	20.0 °C	400 - 480 MPa Show Material materials with Resistencia a la tracción of 400 - 480 MPa
Resistencia a la tracción transversal	20.0 °C	400 MPa Show Material materials with Resistencia a la tracción transversal of 400 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	23.0 °C	371 - 418 J/(kg·K) Show Material materials with Calor específico of 371 - 418 J/(kg·K)	Typical for Wrought Copper Brass
Coeficiente de dilatación térmica	200.0 °C	2.04E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.04E-5 1/K
Conductividad térmica	20.0 °C	109 W/(m·K) Show Material materials with Conductividad térmica of 109 W/(m·K)
Temperatura de fusión		875 - 1075 °C Show Material materials with Temperatura de fusión of 875 - 1075 °C	Typical for Wrought Copper Brass

Eléctrico

Property	Temperature	Value
Conductividad eléctrica	20.0 °C	1.39E+7 S/m Show Material materials with Conductividad eléctrica of 1.39E+7 S/m
Resistividad eléctrica	20.0 °C	7.2E-8 Ω·m Show Material materials with Resistividad eléctrica of 7.2E-8 Ω·m

Chemical properties

Property	Value
Aluminio	0.05 % Show Material materials with Aluminio of 0.05 %
Cobre	59 - 60.5 % Show Material materials with Cobre of 59 - 60.5 %
Estaño	0.2 % Show Material materials with Estaño of 0.2 %
Hierro	0.2 % Show Material materials with Hierro of 0.2 %
Níquel	0.3 % Show Material materials with Níquel of 0.3 %
Plomo	0.2 - 0.8 % Show Material materials with Plomo of 0.2 - 0.8 %

Looking for suppliers of this material? Click to see 3 supplier of EN 1652 Grade CuZn39Pb0.5 R400 on Matmatch