EN 1652 Grade CuCo2Be TH

Want to keep this datasheet? Save it now in your required format

Description

Cuco2Be, mat. No CW104C, is counted among hardenable, low alloyed copper alloys. To the comparable make Cuco2Be, mat. No 2.1285, acc. to DIN 17666 : 1983-12 applies: CuCo2Be achieves compared to CuBe2 at slightly lower hardness and strength values higher electrical and thermal conductivity. The temperature for removal of workhardening approximates 500°C, high corrosion resistance. Processing properties: hot and cold forming: good machinability: moderately hard and soft soldering: good gas shielded welding: good burnishing: good Application: In relay and switch construction for high loadable, live springs and for radiant heaters at semi conductors. Furthermore for resistance and welding electrodes as well as for pistons, plunger and punching tools. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value
Densidad	20.0 °C	8.8 - 8.9 g/cm³ Show Material materials with Densidad of 8.8 - 8.9 g/cm³

Mecánica

Property	Temperature	Value
Dureza Brinell	20.0 °C	100 - 240 [-] Show Material materials with Dureza Brinell of 100 - 240 [-]
Dureza Vickers	20.0 °C	105 - 290 [-] Show Material materials with Dureza Vickers of 105 - 290 [-]
Elongación	20.0 °C	2 - 10 % Show Material materials with Elongación of 2 - 10 %
Elongación A50	20.0 °C	5 - 8 % Show Material materials with Elongación A50 of 5 - 8 %
Elongation A10	20.0 °C	4 - 6 % Show Material materials with Elongation A10 of 4 - 6 %
Elongation A100	20.0 °C	3 - 5 % Show Material materials with Elongation A100 of 3 - 5 %
Límite elástico Rp 0,2	20.0 °C	330 - 970 MPa Show Material materials with Límite elástico Rp 0,2 of 330 - 970 MPa
Módulo elástico	20.0 °C	138 - 140 GPa Show Material materials with Módulo elástico of 138 - 140 GPa
Resistencia a la tracción	20.0 °C	400 - 1040 MPa Show Material materials with Resistencia a la tracción of 400 - 1040 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	23.0 °C	360 - 420 J/(kg·K) Show Material materials with Calor específico of 360 - 420 J/(kg·K)	Typical for Wrought Copper High Copper Alloy
Coeficiente de dilatación térmica	300.0 °C	1.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.8E-5 1/K
Conductividad térmica	20.0 °C	192 - 239 W/(m·K) Show Material materials with Conductividad térmica of 192 - 239 W/(m·K)
Temperatura de fusión		855 - 1090 °C Show Material materials with Temperatura de fusión of 855 - 1090 °C	Typical for Wrought Copper High Copper Alloy
Temperatura máx. de funcionamiento, largo		0 - 350 °C Show Material materials with Temperatura máx. de funcionamiento, largo of 0 - 350 °C

Eléctrico

Property	Temperature	Value
Conductividad eléctrica	20.0 °C	2.50E+7 - 3.20E+7 S/m Show Material materials with Conductividad eléctrica of 2.50E+7 - 3.20E+7 S/m
Specific Electrical conductivity		48 % IACS Show Material materials with Specific Electrical conductivity of 48 % IACS

Chemical properties

Property	Value
Berilio	0.4 - 0.7 % Show Material materials with Berilio of 0.4 - 0.7 %
Cobalto	2 - 2.8 % Show Material materials with Cobalto of 2 - 2.8 %
Hierro	0.2 % Show Material materials with Hierro of 0.2 %
Níquel	0.3 % Show Material materials with Níquel of 0.3 %

Looking for suppliers of this material? Click to see 3 supplier of EN 1652 Grade CuCo2Be TH on Matmatch