Description

Material CuZn39Pb0,5, mat. No. CW610N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb0,5, mat. No. 2.0372 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: moderately machinability: good hard soldering: moderately soft soldering: very good TIG-welding: moderately burnishing: very good Application: For plug pins, fitting parts, rivets, condenser plates, floor plate screeding and drawing instruments.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Propiedades

Mecánica

Property	Temperature	Value	Comment
Elongación	20.0 °C	8 % Show Material materials with Elongación of 8 %
Elongation A10	20.0 °C	6 % Show Material materials with Elongation A10 of 6 %
Límite elástico Rp 0,2	20.0 °C	420 MPa Show Material materials with Límite elástico Rp 0,2 of 420 MPa
Módulo de cizallamiento	23.0 °C	40 GPa Show Material materials with Módulo de cizallamiento of 40 GPa	Typical for Wrought Copper Brass
Módulo elástico	23.0 °C	100 - 125 GPa Show Material materials with Módulo elástico of 100 - 125 GPa	Typical for Wrought Copper Brass
Resistencia a la tracción	20.0 °C	550 MPa Show Material materials with Resistencia a la tracción of 550 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	23.0 °C	371 - 418 J/(kg·K) Show Material materials with Calor específico of 371 - 418 J/(kg·K)	Typical for Wrought Copper Brass
Coeficiente de dilatación térmica	23.0 °C	1.7E-5 - 2.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.7E-5 - 2.1E-5 1/K	Typical for Wrought Copper Brass
Conductividad térmica	23.0 °C	100 - 234 W/(m·K) Show Material materials with Conductividad térmica of 100 - 234 W/(m·K)	Typical for Wrought Copper Brass
Temperatura de fusión		875 - 1075 °C Show Material materials with Temperatura de fusión of 875 - 1075 °C	Typical for Wrought Copper Brass

Chemical properties

Property	Value
Aluminio	0.05 % Show Material materials with Aluminio of 0.05 %
Cobre	59 - 60.5 % Show Material materials with Cobre of 59 - 60.5 %
Estaño	0.2 % Show Material materials with Estaño of 0.2 %
Hierro	0.2 % Show Material materials with Hierro of 0.2 %
Níquel	0.3 % Show Material materials with Níquel of 0.3 %
Plomo	0.2 - 0.8 % Show Material materials with Plomo of 0.2 - 0.8 %

Looking for suppliers of this material? Click to see 3 supplier of EN 12164 Grade CuZn39Pb0.5 R550 on Matmatch