Propiedades
General
| Property | Temperature | Value |
|---|---|---|
Densidad | 20.0 °C | 8.8 - 8.9 g/cm³ Show Material materials with Densidad of 8.8 - 8.9 g/cm³ |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 20.0 °C | 10 - 12 % Show Material materials with Elongación of 10 - 12 % | |
Elongation A100 | 20.0 °C | 3 - 8 % Show Material materials with Elongation A100 of 3 - 8 % | |
Elongation A11.3 | 20.0 °C | 5 - 10 % Show Material materials with Elongation A11.3 of 5 - 10 % | |
Límite elástico Rp 0,2 | 20.0 °C | 540 MPa Show Material materials with Límite elástico Rp 0,2 of 540 MPa | |
Módulo elástico | 23.0 °C | 110 - 130 GPa Show Material materials with Módulo elástico of 110 - 130 GPa | Typical for Wrought Copper High Copper Alloy |
Resistencia a la tracción | 20.0 °C | 590 MPa Show Material materials with Resistencia a la tracción of 590 MPa |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 20.0 °C | 377 J/(kg·K) Show Material materials with Calor específico of 377 J/(kg·K) | |
Coeficiente de dilatación térmica | 300.0 °C | 1.68E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.68E-5 1/K | |
Temperatura de fusión | 855 - 1090 °C Show Material materials with Temperatura de fusión of 855 - 1090 °C | Typical for Wrought Copper High Copper Alloy |
Eléctrico
| Property | Temperature | Value |
|---|---|---|
Conductividad eléctrica | 20.0 °C | 2.20E+7 S/m Show Material materials with Conductividad eléctrica of 2.20E+7 S/m |
Specific Electrical conductivity | 38 % IACS Show Material materials with Specific Electrical conductivity of 38 % IACS |
Chemical properties
| Property | Value |
|---|---|
Hierro | 0.2 % Show Material materials with Hierro of 0.2 % |
Manganeso | 0.1 % Show Material materials with Manganeso of 0.1 % |
Níquel | 1 - 1.6 % Show Material materials with Níquel of 1 - 1.6 % |
Plomo | 0.02 % Show Material materials with Plomo of 0.02 % |
Silicona | 0.4 - 0.7 % Show Material materials with Silicona of 0.4 - 0.7 % |