Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.78 g/cm³ Show Material materials with Densidad of 2.78 g/cm³ | T4 | AA Standards, ASTM B209, ASTM B211 |
2.78 g/cm³ Show Material materials with Densidad of 2.78 g/cm³ | T4 | ||
3.0 g/cm³ Show Material materials with Densidad of 3.0 g/cm³ | T4 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 140.0 MPa Show Material materials with Bending Fatigue Strength of 140.0 MPa | T4 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Dureza Brinell | 120.0 [-] Show Material materials with Dureza Brinell of 120.0 [-] | T4 | AA Standards | ||
Elongación | -195 °C | 19 % Show Material materials with Elongación of 19 % | T4 | Elongation in 50 mm | |
-80 °C | 19 % Show Material materials with Elongación of 19 % | T4 | Elongation in 50 mm | ||
9.0 % Show Material materials with Elongación of 9.0 % | T4 | AA Standards, ASTM B211 | A100 | ||
10.0 % Show Material materials with Elongación of 10.0 % | T4 | AA Standards, ASTM B211 | A50 | ||
12.0 % Show Material materials with Elongación of 12.0 % | T4 | AA Standards, ASTM B209 | A50 | ||
15.0 % Show Material materials with Elongación of 15.0 % | T4 | AA Standards, ASTM B209 | A50 | ||
16.0 % Show Material materials with Elongación of 16.0 % | T4 | ||||
17.0 % Show Material materials with Elongación of 17.0 % | T4 | AA Standards | A100 | ||
0 °C | 19 % Show Material materials with Elongación of 19 % | T4 | Elongation in 50 mm | ||
20.0 % Show Material materials with Elongación of 20.0 % | T4 | AA Standards | A50 | ||
24 °C | 19 % Show Material materials with Elongación of 19 % | T4 | Elongation in 50 mm | ||
100 °C | 19 % Show Material materials with Elongación of 19 % | T4 | Elongation in 50 mm | ||
150 °C | 17 % Show Material materials with Elongación of 17 % | T4 | Elongation in 50 mm | ||
205 °C | 27 % Show Material materials with Elongación of 27 % | T4 | Elongation in 50 mm | ||
260 °C | 55 % Show Material materials with Elongación of 55 % | T4 | Elongation in 50 mm | ||
315 °C | 75 % Show Material materials with Elongación of 75 % | T4 | Elongation in 50 mm | ||
370 °C | 100 % Show Material materials with Elongación of 100 % | T4 | Elongation in 50 mm | ||
Límite elástico | -80 °C | 338 MPa Show Material materials with Límite elástico of 338 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
260.0 MPa Show Material materials with Límite elástico of 260.0 MPa | T4 | AA Standards, ASTM B211 | RP02 | ||
275.0 MPa Show Material materials with Límite elástico of 275.0 MPa | T4 | AA Standards, ASTM B209, ASTM B211 | RP02 | ||
290.0 MPa Show Material materials with Límite elástico of 290.0 MPa | T4 | AA Standards, ASTM B211 | RP02 | ||
310.0 MPa Show Material materials with Límite elástico of 310.0 MPa | T4 | AA Standards, ASTM B211 | RP02 | ||
320.0 MPa Show Material materials with Límite elástico of 320.0 MPa | T4 | ||||
0 °C | 324 MPa Show Material materials with Límite elástico of 324 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
325.0 MPa Show Material materials with Límite elástico of 325.0 MPa | T4 | AA Standards | RP02 | ||
24 °C | 324 MPa Show Material materials with Límite elástico of 324 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 310 MPa Show Material materials with Límite elástico of 310 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
150 °C | 248 MPa Show Material materials with Límite elástico of 248 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
205 °C | 131 MPa Show Material materials with Límite elástico of 131 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
315 °C | 41 MPa Show Material materials with Límite elástico of 41 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
370 °C | 28 MPa Show Material materials with Límite elástico of 28 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 28.0 GPa Show Material materials with Módulo de cizallamiento of 28.0 GPa | T4 | |||
Módulo elástico | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T4 | AA Standards, ASTM B209, ASTM B211 | ||
73 GPa Show Material materials with Módulo elástico of 73 GPa | T4 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Resistencia a la tracción | -195 °C | 580 MPa Show Material materials with Resistencia a la tracción of 580 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 490 MPa Show Material materials with Resistencia a la tracción of 490 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
425.0 MPa Show Material materials with Resistencia a la tracción of 425.0 MPa | T4 | AA Standards, ASTM B209, ASTM B211 | |||
472.0 MPa Show Material materials with Resistencia a la tracción of 472.0 MPa | T4 | AA Standards | |||
0 °C | 475 MPa Show Material materials with Resistencia a la tracción of 475 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
480.0 MPa Show Material materials with Resistencia a la tracción of 480.0 MPa | T4 | ||||
24 °C | 470 MPa Show Material materials with Resistencia a la tracción of 470 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 435 MPa Show Material materials with Resistencia a la tracción of 435 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 310 MPa Show Material materials with Resistencia a la tracción of 310 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 180 MPa Show Material materials with Resistencia a la tracción of 180 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 75 MPa Show Material materials with Resistencia a la tracción of 75 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | T4 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 870.0 J/(kg·K) Show Material materials with Calor específico of 870.0 J/(kg·K) | T4 | ||
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | T4 | ||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K | T4 | AA Standards, ASTM B209, ASTM B211 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K | T4 | AA Standards, ASTM B209, ASTM B211 | |
Conductividad térmica | 120.0 W/(m·K) Show Material materials with Conductividad térmica of 120.0 W/(m·K) | T4 | ||
121.0 - 193.0 W/(m·K) Show Material materials with Conductividad térmica of 121.0 - 193.0 W/(m·K) | T4 | AA Standards, ASTM B209, ASTM B211 | ||
Temperatura de fusión | 500.0 °C Show Material materials with Temperatura de fusión of 500.0 °C | T4 | ||
505.0 - 635.0 °C Show Material materials with Temperatura de fusión of 505.0 - 635.0 °C | T4 | AA Standards, ASTM B209, ASTM B211 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 17000000.0 - 29000000.0 S/m Show Material materials with Conductividad eléctrica of 17000000.0 - 29000000.0 S/m | T4 | AA Standards, ASTM B209, ASTM B211 | |
17000000 S/m Show Material materials with Conductividad eléctrica of 17000000 S/m | T4 | Typical value | ||
Resistividad eléctrica | 3.45e-08 - 5.88e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.45e-08 - 5.88e-08 Ω·m | T4 | AA Standards, ASTM B209, ASTM B211 | |
5.7e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.7e-08 Ω·m | T4 | Typical value | ||
Specific Electrical conductivity | 29.0 % IACS Show Material materials with Specific Electrical conductivity of 29.0 % IACS | T4 | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 90.7 - 94.7 % Show Material materials with Aluminio of 90.7 - 94.7 % | T4 | |
Circonio | 0.2 % Show Material materials with Circonio of 0.2 % | T4 | |
Cobre | 3.8 - 4.9 % Show Material materials with Cobre of 3.8 - 4.9 % | T4 | AA Standards, ASTM B209, ASTM B211 |
Cromo | 0.1 % Show Material materials with Cromo of 0.1 % | T4 | AA Standards, ASTM B209, ASTM B211 |
Hierro | 0.50 % Show Material materials with Hierro of 0.50 % | T4 | AA Standards, ASTM B209, ASTM B211 |
0.5 % Show Material materials with Hierro of 0.5 % | T4 | ||
Magnesio | 1.2 - 1.8 % Show Material materials with Magnesio of 1.2 - 1.8 % | T4 | AA Standards, ASTM B209, ASTM B211 |
Manganeso | 0.3 - 0.9 % Show Material materials with Manganeso of 0.3 - 0.9 % | T4 | AA Standards, ASTM B209, ASTM B211 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T4 | |
Silicona | 0.5 % Show Material materials with Silicona of 0.5 % | T4 | AA Standards, ASTM B209, ASTM B211 |
Titanio | 0.15 % Show Material materials with Titanio of 0.15 % | T4 | AA Standards, ASTM B209, ASTM B211 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T4 | AA Standards, ASTM B209, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T4,T3, T351, T3510, T3511), d (T6, T861, T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): poor(T4, T3, T351, T3510, T3511, T6), not suitable (T361, T861, T81, T851, T8510, T8511) | |