Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.84 g/cm³ Show Material materials with Densidad of 2.84 g/cm³ | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
2.84 g/cm³ Show Material materials with Densidad of 2.84 g/cm³ | T62 | ||
3.1 g/cm³ Show Material materials with Densidad of 3.1 g/cm³ | T62 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa | T62 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Elongación | -195 °C | 16 % Show Material materials with Elongación of 16 % | T62 | Elongation in 50 mm | |
-80 °C | 13 % Show Material materials with Elongación of 13 % | T62 | Elongation in 50 mm | ||
5.0 % Show Material materials with Elongación of 5.0 % | T62 | AA Standards, ASTM B221, ASTM B241 | A100 | ||
6.0 % Show Material materials with Elongación of 6.0 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | A50 | ||
6.0 % Show Material materials with Elongación of 6.0 % | T62 | AA Standards, ASTM B209 | A100 | ||
7.0 % Show Material materials with Elongación of 7.0 % | T62 | AA Standards, ASTM B209 | A50 | ||
7.0 % Show Material materials with Elongación of 7.0 % | T62 | AA Standards, ASTM B209 | A100 | ||
8.0 % Show Material materials with Elongación of 8.0 % | T62 | AA Standards, ASTM B209 | A50 | ||
8.2 % Show Material materials with Elongación of 8.2 % | T62 | ||||
10.0 % Show Material materials with Elongación of 10.0 % | T62 | AA Standards | A50 | ||
0 °C | 12 % Show Material materials with Elongación of 12 % | T62 | Elongation in 50 mm | ||
24 °C | 12 % Show Material materials with Elongación of 12 % | T62 | Elongation in 50 mm | ||
100 °C | 14 % Show Material materials with Elongación of 14 % | T62 | Elongation in 50 mm | ||
150 °C | 17 % Show Material materials with Elongación of 17 % | T62 | Elongation in 50 mm | ||
205 °C | 20 % Show Material materials with Elongación of 20 % | T62 | Elongation in 50 mm | ||
260 °C | 21 % Show Material materials with Elongación of 21 % | T62 | Elongation in 50 mm | ||
315 °C | 40 % Show Material materials with Elongación of 40 % | T62 | Elongation in 50 mm | ||
370 °C | 75 % Show Material materials with Elongación of 75 % | T62 | Elongation in 50 mm | ||
Límite elástico | 250.0 MPa Show Material materials with Límite elástico of 250.0 MPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | RP02 | |
290.0 MPa Show Material materials with Límite elástico of 290.0 MPa | T62 | AA Standards | RP02 | ||
290.0 MPa Show Material materials with Límite elástico of 290.0 MPa | T62 | ||||
Módulo de cizallamiento | 26.0 GPa Show Material materials with Módulo de cizallamiento of 26.0 GPa | T62 | |||
Módulo elástico | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
73 GPa Show Material materials with Módulo elástico of 73 GPa | T62 | ||||
74.0 GPa Show Material materials with Módulo elástico of 74.0 GPa | T62 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Resistencia a la tracción | -195 °C | 503 MPa Show Material materials with Resistencia a la tracción of 503 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 435 MPa Show Material materials with Resistencia a la tracción of 435 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370.0 MPa Show Material materials with Resistencia a la tracción of 370.0 MPa | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |||
415.0 MPa Show Material materials with Resistencia a la tracción of 415.0 MPa | T62 | AA Standards | |||
0 °C | 415 MPa Show Material materials with Resistencia a la tracción of 415 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
420.0 MPa Show Material materials with Resistencia a la tracción of 420.0 MPa | T62 | ||||
24 °C | 400 MPa Show Material materials with Resistencia a la tracción of 400 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 372 MPa Show Material materials with Resistencia a la tracción of 372 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 310 MPa Show Material materials with Resistencia a la tracción of 310 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 235 MPa Show Material materials with Resistencia a la tracción of 235 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 185 MPa Show Material materials with Resistencia a la tracción of 185 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 70 MPa Show Material materials with Resistencia a la tracción of 70 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 30 MPa Show Material materials with Resistencia a la tracción of 30 MPa | T62 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 860.0 J/(kg·K) Show Material materials with Calor específico of 860.0 J/(kg·K) | T62 | ||
Coeficiente de dilatación térmica | 2.2e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2e-05 1/K | T62 | ||
20 °C | 2.23e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.23e-05 1/K | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
100 °C | 2.23e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.23e-05 1/K | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
Conductividad térmica | 113.0 - 172.0 W/(m·K) Show Material materials with Conductividad térmica of 113.0 - 172.0 W/(m·K) | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
140.0 W/(m·K) Show Material materials with Conductividad térmica of 140.0 W/(m·K) | T62 | |||
Temperatura de fusión | 540.0 °C Show Material materials with Temperatura de fusión of 540.0 °C | T62 | ||
545.0 - 645.0 °C Show Material materials with Temperatura de fusión of 545.0 - 645.0 °C | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 16000000.0 - 26000000.0 S/m Show Material materials with Conductividad eléctrica of 16000000.0 - 26000000.0 S/m | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
17000000 S/m Show Material materials with Conductividad eléctrica of 17000000 S/m | T62 | Typical/derived value | ||
Resistividad eléctrica | 3.85e-08 - 6.25e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.85e-08 - 6.25e-08 Ω·m | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
6.2e-08 Ω·m Show Material materials with Resistividad eléctrica of 6.2e-08 Ω·m | T62 | Typical value | ||
Specific Electrical conductivity | 30.0 % IACS Show Material materials with Specific Electrical conductivity of 30.0 % IACS | T62 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 91.5 - 93.8 % Show Material materials with Aluminio of 91.5 - 93.8 % | T62 | |
Circonio | 0.1 - 0.25 % Show Material materials with Circonio of 0.1 - 0.25 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Cobre | 5.8 - 6.8 % Show Material materials with Cobre of 5.8 - 6.8 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Hierro | 0.30 % Show Material materials with Hierro of 0.30 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
0.3 % Show Material materials with Hierro of 0.3 % | T62 | ||
Magnesio | 0.02 % Show Material materials with Magnesio of 0.02 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Manganeso | 0.2 - 0.4 % Show Material materials with Manganeso of 0.2 - 0.4 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T62 | |
Silicona | 0.2 % Show Material materials with Silicona of 0.2 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Titanio | 0.02 - 0.1 % Show Material materials with Titanio of 0.02 - 0.1 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Vanadio | 0.05 - 0.15 % Show Material materials with Vanadio of 0.05 - 0.15 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T62 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T31, T351, T3510, T3511, T37), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): poor(T31, T351, T3510, T3511), not suitable (T37, T81, T851, T8510, T8511, T87) | |