Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.84 g/cm³ Show Material materials with Densidad of 2.84 g/cm³ | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
2.84 g/cm³ Show Material materials with Densidad of 2.84 g/cm³ | T81 | ||
3.1 g/cm³ Show Material materials with Densidad of 3.1 g/cm³ | T81 |
Mecánica
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 105.0 MPa Show Material materials with Bending Fatigue Strength of 105.0 MPa | T81 | AA Standards | ||
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Elongación | 5.0 % Show Material materials with Elongación of 5.0 % | T81 | AA Standards, ASTM B221, ASTM B241 | A100 | |
6.0 % Show Material materials with Elongación of 6.0 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | A50 | ||
7.0 % Show Material materials with Elongación of 7.0 % | T81 | AA Standards, ASTM B209 | A50 | ||
8.2 % Show Material materials with Elongación of 8.2 % | T81 | ||||
10.0 % Show Material materials with Elongación of 10.0 % | T81 | AA Standards | A50 | ||
10 % Show Material materials with Elongación of 10 % | T81 | ||||
Límite elástico | -196 °C | 421 MPa Show Material materials with Límite elástico of 421 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 372 MPa Show Material materials with Límite elástico of 372 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 359 MPa Show Material materials with Límite elástico of 359 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
290.0 MPa Show Material materials with Límite elástico of 290.0 MPa | T81 | AA Standards, ASTM B221, ASTM B241 | RP02 | ||
315.0 MPa Show Material materials with Límite elástico of 315.0 MPa | T81 | AA Standards, ASTM B209 | RP02 | ||
350.0 MPa Show Material materials with Límite elástico of 350.0 MPa | T81 | AA Standards | RP02 | ||
350.0 MPa Show Material materials with Límite elástico of 350.0 MPa | T81 | ||||
24 °C | 345 MPa Show Material materials with Límite elástico of 345 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 324 MPa Show Material materials with Límite elástico of 324 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 276 MPa Show Material materials with Límite elástico of 276 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 200 MPa Show Material materials with Límite elástico of 200 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 159 MPa Show Material materials with Límite elástico of 159 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 41 MPa Show Material materials with Límite elástico of 41 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 26 MPa Show Material materials with Límite elástico of 26 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Módulo de cizallamiento | 26.0 GPa Show Material materials with Módulo de cizallamiento of 26.0 GPa | T81 | |||
Módulo elástico | 73.0 GPa Show Material materials with Módulo elástico of 73.0 GPa | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | ||
73 GPa Show Material materials with Módulo elástico of 73 GPa | T81 | ||||
74.0 GPa Show Material materials with Módulo elástico of 74.0 GPa | T81 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Resistencia a la tracción | -195 °C | 572 MPa Show Material materials with Resistencia a la tracción of 572 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 490 MPa Show Material materials with Resistencia a la tracción of 490 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
400.0 MPa Show Material materials with Resistencia a la tracción of 400.0 MPa | T81 | AA Standards, ASTM B221, ASTM B241 | |||
425.0 MPa Show Material materials with Resistencia a la tracción of 425.0 MPa | T81 | AA Standards, ASTM B209 | |||
455.0 MPa Show Material materials with Resistencia a la tracción of 455.0 MPa | T81 | AA Standards | |||
470.0 MPa Show Material materials with Resistencia a la tracción of 470.0 MPa | T81 | ||||
0 °C | 475 MPa Show Material materials with Resistencia a la tracción of 475 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 455 MPa Show Material materials with Resistencia a la tracción of 455 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 415 MPa Show Material materials with Resistencia a la tracción of 415 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 338 MPa Show Material materials with Resistencia a la tracción of 338 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 248 MPa Show Material materials with Resistencia a la tracción of 248 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 200 MPa Show Material materials with Resistencia a la tracción of 200 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 48 MPa Show Material materials with Resistencia a la tracción of 48 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 30 MPa Show Material materials with Resistencia a la tracción of 30 MPa | T81 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 860.0 J/(kg·K) Show Material materials with Calor específico of 860.0 J/(kg·K) | T81 | ||
Coeficiente de dilatación térmica | 2.2e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2e-05 1/K | T81 | ||
20 °C | 2.23e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.23e-05 1/K | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
100 °C | 2.23e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.23e-05 1/K | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
Conductividad térmica | 113.0 - 172.0 W/(m·K) Show Material materials with Conductividad térmica of 113.0 - 172.0 W/(m·K) | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
120.0 W/(m·K) Show Material materials with Conductividad térmica of 120.0 W/(m·K) | T81 | |||
Temperatura de fusión | 540.0 °C Show Material materials with Temperatura de fusión of 540.0 °C | T81 | ||
545.0 - 645.0 °C Show Material materials with Temperatura de fusión of 545.0 - 645.0 °C | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Eléctrico
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Conductividad eléctrica | 16000000.0 - 26000000.0 S/m Show Material materials with Conductividad eléctrica of 16000000.0 - 26000000.0 S/m | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
17000000 S/m Show Material materials with Conductividad eléctrica of 17000000 S/m | T81 | Typical value | ||
Resistividad eléctrica | 3.85e-08 - 6.25e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.85e-08 - 6.25e-08 Ω·m | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 | |
5.8e-08 Ω·m Show Material materials with Resistividad eléctrica of 5.8e-08 Ω·m | T81 | Typical value | ||
Specific Electrical conductivity | 29.0 % IACS Show Material materials with Specific Electrical conductivity of 29.0 % IACS | T81 | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 91.5 - 93.8 % Show Material materials with Aluminio of 91.5 - 93.8 % | T81 | |
Circonio | 0.1 - 0.25 % Show Material materials with Circonio of 0.1 - 0.25 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Cobre | 5.8 - 6.8 % Show Material materials with Cobre of 5.8 - 6.8 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Hierro | 0.30 % Show Material materials with Hierro of 0.30 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
0.3 % Show Material materials with Hierro of 0.3 % | T81 | ||
Magnesio | 0.02 % Show Material materials with Magnesio of 0.02 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Manganeso | 0.2 - 0.4 % Show Material materials with Manganeso of 0.2 - 0.4 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | T81 | |
Silicona | 0.2 % Show Material materials with Silicona of 0.2 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Titanio | 0.02 - 0.1 % Show Material materials with Titanio of 0.02 - 0.1 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Vanadio | 0.05 - 0.15 % Show Material materials with Vanadio of 0.05 - 0.15 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | T81 | AA Standards, ASTM B209, ASTM B221, ASTM B241 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T31, T351, T3510, T3511, T37), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): poor(T31, T351, T3510, T3511), not suitable (T37, T81, T851, T8510, T8511, T87) | |