Propiedades
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.73 g/cm³ Show Material materials with Densidad of 2.73 g/cm³ | H113 | AA Standards, ASTM B210, ASTM B483 |
2.8 g/cm³ Show Material materials with Densidad of 2.8 g/cm³ | H113 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||
Elongación | 14.0 % Show Material materials with Elongación of 14.0 % | H113 | ||
Límite elástico | 35.0 MPa Show Material materials with Límite elástico of 35.0 MPa | H113 | AA Standards, ASTM B210, ASTM B483 | RP02 |
40.0 MPa Show Material materials with Límite elástico of 40.0 MPa | H113 | |||
Módulo de cizallamiento | 25.0 - 26.0 GPa Show Material materials with Módulo de cizallamiento of 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||
Módulo elástico | 69.0 GPa Show Material materials with Módulo elástico of 69.0 GPa | H113 | AA Standards, ASTM B210, ASTM B483 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||
Resistencia a la tracción | 95.0 MPa Show Material materials with Resistencia a la tracción of 95.0 MPa | H113 | AA Standards, ASTM B210, ASTM B483 | |
110.0 MPa Show Material materials with Resistencia a la tracción of 110.0 MPa | H113 |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Calor específico | 890.0 J/(kg·K) Show Material materials with Calor específico of 890.0 J/(kg·K) | H113 | ||
Coeficiente de dilatación térmica | 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3e-05 1/K | H113 | ||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K | H113 | AA Standards, ASTM B210, ASTM B483 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3199999999999998e-05 1/K | H113 | AA Standards, ASTM B210, ASTM B483 | |
Conductividad térmica | 159.0 - 193.0 W/(m·K) Show Material materials with Conductividad térmica of 159.0 - 193.0 W/(m·K) | H113 | AA Standards, ASTM B210, ASTM B483 | |
180.0 W/(m·K) Show Material materials with Conductividad térmica of 180.0 W/(m·K) | H113 | |||
Temperatura de fusión | 640.0 - 655.0 °C Show Material materials with Temperatura de fusión of 640.0 - 655.0 °C | H113 | AA Standards, ASTM B210, ASTM B483 | |
640.0 °C Show Material materials with Temperatura de fusión of 640.0 °C | H113 |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 24000000.0 - 29000000.0 S/m Show Material materials with Conductividad eléctrica of 24000000.0 - 29000000.0 S/m | H113 | AA Standards, ASTM B210, ASTM B483 |
Resistividad eléctrica | 3.45e-08 - 4.17e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.45e-08 - 4.17e-08 Ω·m | H113 | AA Standards, ASTM B210, ASTM B483 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminio | 96.8 - 99.0 % Show Material materials with Aluminio of 96.8 - 99.0 % | H113 | |
Cobre | 0.05 - 0.2 % Show Material materials with Cobre of 0.05 - 0.2 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Hierro | 0.70 % Show Material materials with Hierro of 0.70 % | H113 | AA Standards, ASTM B210, ASTM B483 |
0.7 % Show Material materials with Hierro of 0.7 % | H113 | ||
Manganeso | 1.0 - 1.5 % Show Material materials with Manganeso of 1.0 - 1.5 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Otro | 0.15 % Show Material materials with Otro of 0.15 % | H113 | |
Silicona | 0.6 % Show Material materials with Silicona of 0.6 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H113 | AA Standards, ASTM B210, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H25) | |
| Workability | general (condition): good (O, H12), acceptable (H14, H25), poor(H16, H18) | |